建立了电磁离心凝固过程熔体动量传递、传热和传质耦合数学模型,模拟计算了熔体在不同感应强度下的流动速度.计算结果表明,熔体在电磁力的作用下产生与铸模转动方向相反的流动,流动速度呈周期性分布,并且在凝固前沿达到最大随着磁感应强度的增加,熔体流动速度达到的最大值也愈大.使用有限元软件ANSYS,把熔体流动计算结果作为参数,计算了枝晶的受力状态通过计算表明,熔体流过枝晶会在枝晶周围产生很大的速度变化,流体对枝晶的冲刷可使枝晶产生机械折断.电磁搅拌通过增加断裂枝晶数量促进柱状晶-等轴晶转变.
参考文献
| [1] | Southin R T. Trans TMS-AIME, 1967; 239:220 |
| [2] | Jackson K A, Hunt J D, Uhlmam D R. Trans TMS-AIME, 1966; 236:149 |
| [3] | Ohno A. The Solidification of Metals. Chijin: ShokanCo. Ltd., 1976:50 |
| [4] | HellaWell A, Liu S, Lu S Z. JOM, 1997; 49:34 |
| [5] | Dahle A K, Thevik H J, Arnberg L, John D H St. MetallMater Trans, 1999; 30B: 287 |
| [6] | Pilling J, Hellawell A. Metall Mater Trans, 1996; 27A: 229 |
| [7] | Dahle A K, Arnberg L. JOM, 1996; 48:34 |
| [8] | Dahle A K, Arnberg L. Acta Mater, 1997; 45:547 |
| [9] | Yang Y S, Liu Q M, Jiao Y N, Ge Y L, Hu Z Q, Gao YY, Jia G L, Zhang J S. ISIJ Int, 1995; 35:389 |
| [10] | Perie R, Ruth J C. Iron Steelmaker, 1977; 4(2): 24 |
| [11] | Neilson D G, Incropera F P. Int J Heat Mass Transfer,1990; 33:367 |
| [12] | Chang S, Stefanescu D M. Metall Trans Mater, 1996; 27A: 2708 |
| [13] | Diao Q Z, Tsai H L. Metall Trans, 1993; 24A: 963 |
| [14] | Vives C, Perry C. Int J Heat Mass Transfer, 1987; 30:479 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%