依据非晶态合金与其相关相具有相近的电子浓度的规律,对Zr-Al-Ni-Cu系进行了电子浓度e/a=1.38的块状非晶成分的设计和制备.获得的块状非晶具有107 K的大过冷度,表征非晶形成能力(GFA)的Trg值在0.58-0.64之间,最佳成分为Zr60 6Al11.4Ni15.5Cu12 5,其GFA和热稳定性优于Inoue非晶合金.在相同电子浓度下,平均原子尺寸Ra=0.1486nm,其GFA优于Ra为0.1496和0.1506 nm的合金,表明原子尺寸因素对非晶形成能力有重要影响.
参考文献
[1] | Inoue A, Zhang T, Masumoto T. Mater Trans JIM, 1989;30:965 |
[2] | Inoue A, Kita K, Zhang T, Masumoto T. Non-CrystSolids, 1993; 156-158:473 |
[3] | Peker A L, Johnson W L. Appl Phys Lett, 1993; 63, 2342 |
[4] | Inoue A, Zhang T. Masumoto J. Non-Cryst Solids, 1993;156-158:473 |
[5] | Inoue A. Mater Sci Forum, 1995; 691:179-181 |
[6] | Nagel S R, Tauc J. Phys Rev Lett, 1975; 35:380 |
[7] | Haussler P. Phys Rep, 1992; 222(2): 65 |
[8] | Hafner J, Krajci M. Phys Rev, 1993; B47:11795 |
[9] | Mizutani U, Takeuchi T. Sato Prog Mater Sci, 2003, inPress |
[10] | Shek C H, Wang Y M, Dong C. Mater Sci Eng, 2000;A291:78 |
[11] | Wang Y M, Qiang J B, Wong H C, Shek C H, Dong C. J Mater Res, 2003; 18:642 |
[12] | Chen W R, Wang Y M, Qiang J B, Dong C. Acta Metall Sin, 2002; 38:421(陈伟荣,王英敏,羌建兵,董闯.金属学报,2002;38:421) |
[13] | Chen W R. Ph D Thesis, Dalian: Dalian University of Technol, 2002(陈伟学.大连理工大学博士论文,大连,2002) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%