采用动力学分析方法(DMA)、电阻法和透射电镜(TEM),分别测量了Mn-Ni合金的内耗、模量与温度的变化关系和Ms,tn点,观察了合金的显微组织,并与Mn-Cu合金进行了对比分析以研究反铁磁转变、马氏体相变之间的耦合机制,以及反铁磁转变和马氏体相变对孪晶形成的作用.分析结果表明:在Mn-Ni合金中,可以由孪晶峰和马氏体相变峰的叠加产生高阻尼;另外,反铁磁转变与马氏体相变能否紧密耦合,除了与"应变释放机制"相关的畸变度有关外,还与Ms点和tn点之间的差异具有很大的关系.
参考文献
| [1] | Zener C. Elasticity and Anelasticity in Metal. Chicago:Chicago University Press, 1948 |
| [2] | Hicks T J, Pepper A R, Smith J H. J Phys, 1968; 1C: 1638 |
| [3] | Ito K, Kobayashi M, Abe H. Met Sci J, 1979; 11:502 |
| [4] | Ito K, Tsukishima M, Kobayashi M. Trans Jpn Inst Met,1983; 24:487 |
| [5] | Nakanishi N, Nagasawa A, Murakami Y. J Phys Colloq,1981; 43(C4): 35 |
| [6] | Makhurance P, Gaunt P. J Phys, 1969; 2C: 959 |
| [7] | Tsunoda Y, Wakabayashi N. J Phys Soc Jpn, 1981; 50:3341 |
| [8] | Lowde R D, Harley R T, Saunders G A, Sato M, Scherm R, Underhill C. Proc R Soc, London, 1981; A374:87 |
| [9] | Hedley J A. Met Sci J, 1968; 2:129 |
| [10] | Patterson W R. TMS AIME, 1965; 233:438 |
| [11] | Roth W L. J Appl Phys, 1960; 31:2000 |
| [12] | Bean C P, Rodbell C D. Phys Rev, 1962; 126:104 |
| [13] | Hocke U, Warlimont H. J Phys, 1977; 7F: 1145 |
| [14] | Chen S C, Chang C Y, Yan C L, Hsu T Y (Xu Z Y). Mater Sci Eng, 1999; A264:262 |
| [15] | Nishida T. Physica, 1992; 179B: 215 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%