用感应悬浮冷坩锅法制备了单相性良好的Sm0.99Gd0.01Al2多晶金属间化合物.对其低温的声学和比热容性质进行了研究,得到了样品模量和声衰减以及随温度变化的规律.研究表明,在磁相变附近,样品的声学性质有剧烈的反常现象.比热容测量的结果表明这是一个二级相变.结合样品的磁性性质,对其声学特性进行了分析.
参考文献
| [1] | Adachi H, Ino H. Nature, 1999; 401:148 |
| [2] | Adachi H, Kawata H, Hashimoto H, Sato Y, Matsumoto I, Tanaka Y. Phys Rev Lett, 2001; 87:127202-1 |
| [3] | Wang K Q, Zhuang Z Z. Chin J Low Temp Phys, 1996;18:339(王克勤,庄志忠.低温物理学报,1996;18:339) |
| [4] | Wang H F, Wu Z Q. Experimental Methods for Solid State Physics. Beijing: Higher Education Press, 1990:161(王华馥,吴自勤.固体物理实验方法.北京:高等教育出版社,1990: 161) |
| [5] | Nowick A S, Berry B S. Anelastic Relaxation in Crystalline Solids. London: Academic Press, 1972:588 |
| [6] | Qu J F. Thesis for Bachelor's Degree, University of Science and Technology of China, Hefei, 2001(屈继锋.中国科学技术大学学士学位论文,合肥,2001) |
| [7] | Landau L D, Lifshitz E M. Statistical Physics. New York:Pergamon Press, 1958:430 |
| [8] | Landau L D, Khalatnikov S M. Doklady Akad Nauk SSSR,1954; 96:469 |
| [9] | Rosen M. Phys Rev, 1968; 174:504 |
| [10] | Rosen M. Phys Rev, 1969; 180:540 |
| [11] | Bennett H S, Pytte E. Phys Rev, 1967; 155:553 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%