制备了部分Ca替代Y的Y1-xCaxBa2Cu3O7-δ样品,以及通过高温淬火获得了具有不同氧含量的Y0.85Ca0.15Ba2Cu3O7-δ系列陶瓷样品.用双端振动簧法研究了从室温至液氮温区的音频内耗谱.结果表明,未掺杂的YBa2Cu3O7-δ(Y123)在220 K附近有一个内耗峰(记为P3).随着Ca含量的增加,P3峰的强度逐渐受到了抑制,而峰位稍向低温移动.对于以0.15的Ca替代Y的Y123样品,通过高温淬火减少氧含量,P3峰由抑制逐渐恢复.P3峰依赖于载流子的浓度,在过掺杂区P3峰受到抑制,这表明P3峰与高温超导欠掺杂区的异常有关.进一步的分析认为,P3峰很可能联系于欠掺杂区载流子的异常行为.
参考文献
| [1] | Tallon J L, Loram J W. Physica, 2001; 349C: 53 |
| [2] | Cannelli G, Cantelli R, Cordero F, Trequattrini F. Supercond Sci Technol, 1992; 5:247 |
| [3] | Wang Y N, Huang Y N, Shen H M. Supercond Sci Technol,1994; 7:441 |
| [4] | Sharma R P, Ogale S B, Zhang Z H, Liu J R, Chu W K, Weal B, Paulikas A, Zheng H, Venkatesan T. Nature,2000; 404:736 |
| [5] | Brinkmann D. J Mol Struct, 1995; 345:167 |
| [6] | Sergeenkov S, Ausloos M, Mehbod M. J Phys: Condensed Matter, 1994; 6:L373 |
| [7] | Li A, Wang Y N, Ying X N, Zhang Q M, Chen W. M.Supercond Sci Technol, 1999; 12:645 |
| [8] | Titova S G, Arbazova T L, Balakirev V F, Fedorova O M,Pal-Val P P, Pal-Val L N. Low Temp Phys, 1996; 22:938 |
| [9] | Miiller K A. J Supercond, 1999; 12:3 |
| [10] | Zhang L Y, Liu C L, Yang X Q, Han Q. Physica, 2000;279B: 230 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%