采用电磁离心铸造方法制备了1Cr18Ni9Ti不锈钢管坯.在电磁搅拌作用下,管坯铸态微观组织被细化,一次枝晶间距为40μm,与普通离心铸造相比减小70%;管坯的室温屈服强度为274 MPa、延伸率为77%,分别比普通离心铸造管坯提高23%和28%.实验结果表明:电磁离心铸造可明显提高管坯的塑性加工性能,利用电磁离心管坯可直接进行冷轧1Cr18Ni9Ti不锈钢无缝薄壁管,实验得到的最大减薄率大于91.4%.
参考文献
| [1] | Zhong Q X,Yan S X.Steel Pipe,2002;31(5):1(钟倩霞,严圣祥.钢管,2002;31(5):1) . |
| [2] | Zhou Z H.Steel Pipe,2000;29(6):1(邹子和钢管,2000;29(6):1) |
| [3] | Yang Y S, Jiao Y N, Hu Z Q. ISIJ Int, 1995; 35(4): 389 |
| [4] | Yang Y S, Hu Z Q. Z Metallkd, 2000; 91(4): 280 |
| [5] | Guo M H, Yang Y S, Hua F A, Guo D Y, He Y L, Hu Z Q. Mater Eng, 2002; (9): 7(郭明虎,杨院生,花福安,郭大勇,贺幼良,胡壮麒材料工程,2002;(9):7) |
| [6] | Yang Y S,Liu Q M,Jiao Y N,Ge Y L,Hu Z Q.Acta Metall Sin,1995;30(5):208(杨院生,刘清民,焦育宁,葛云龙,胡壮麒.金属学报,1995;30(5): 208) |
| [7] | Kurz W, Fisher D J. Acta Metall, 1981; 29(3): 11 |
| [8] | Cui Z Q. Metallurgy and Heat Treat. Beijing: Machinery Industry Press, 1988:180(崔忠圻.金属学与热处理.北京:机械工业出版社,1988:180) |
| [9] | Zhang W Q,Yang Y S,Liu Q M,Zhu Y F,Zhang Q S,Hu Z Q.Mater Sci Technol,1998;14:306 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%