在直接时效IN718(简称DA718)合金中单独添加磷至0.022%(质量分数,下同)及添加磷至0.022%和硼至0.011%,合金的持久性能都得到了大幅度的提高.其中在650℃/700 MPa,两种成分合金的持久寿命分别提高至200%和280%,但后者的塑性有所下降磷、硼对蠕变实验中的应力指数影响不大,但显著提高表观蠕变激活能对磷、硼在DA718合金中的作用进行了讨论.
参考文献
[1] | Cao W D, Kennedy R L. In: Loria E A ed, Superalloys 718, 625, 706 and Various Derivatives, TMS, 1994:463 |
[2] | Kennedy R L, Cao W D, Thomas W M. Adv Mater Process, 1996; 150(3): 33 |
[3] | Xie X S, Liu X B, Hu Y H, Tang B, Xu Z C, Dong J X, Ni K Q, Zhu Y X, Tien S S, Zhang L P, Xie W. In:Kissinger R D, Deye D J, Anton D L, Cetel A D, Nathal M V, Pollock T M, Woodford D A eds, Superalloys 1996,TMS, 1996:599 |
[4] | Guo S R, Sun W R, Lu D Z, Hu Z Q. In: LoriaE A ed,Superalloys 718, 625, 706 and Various Derivatives, TMS,1997:521 |
[5] | Sun W R, Guo S R, Lu D Z, Hu Z Q. Metall Mater Trans,1997; 28A: 649 |
[6] | Liu X, Dong J X, Tang B, Hu Y, Xie X S. Mater Sci Eng A, 1999; 270:190 |
[7] | Horton J A, McKamey C G, Miller M K, Cao W D,Kennedy R L. In: Loria E A ed, Superalloys 718, 625,706 and Various Derivatives, TMS, 1997:401 |
[8] | McKamey C G, Carmichael C A, Cao W D, Kennedy R L. Scr Mater, 1998; 38:485 |
[9] | Cao W D, Kennedy R L. In: Loria E A ed, Superalloys 718, 625, 706 and Various Derivatives, TMS, 2001:45510 |
[10] | Funkenbusch A W, Heldt L A, Stein D F. Metall Trans,1982; 13A: 611 |
[11] | Yonezawa T, Onimura K, Sakamoto O, Sasaguri N,Nakata H, Susukida H. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors,NACE, Houston, TX, 1984:345 |
[12] | Was G S, Martin G R. Metall Trans, 1985; 16A: 349 |
[13] | Hall E L, Briant C L. Metall Trans A, 1985; 16A: 1225 |
[14] | Braint C L. Metall Trans, 1988; 19A: 137 |
[15] | Miller M K, Horton J A, Cao W D, Kennedy R L. J Phys (France), 1996; 6(5): 241 |
[16] | Song H W. PhD Thesis, Institute of Metal Research, The Chinese Academy of Science, Shenyang, 1999(宋洪伟,博士学位论文,中国科学院金属研究所.1999) |
[17] | Sherby O D. Acta Met, 1962; 10:135 |
[18] | Dorn J E, Mech J. Phys Solids, 1964; 2:85 |
[19] | Weertman J. J Appl Phys, 1957; 28:362 |
[20] | Barrett C R, Nix W D. Acta Met, 1965; 13:1247 |
[21] | Nabarro F R N. Report of Conference on Strength of Solids, The Physical Society, Bristol, England, 1948:75 |
[22] | Song H W, GuoS R, Lu D Z, XuY, WangYL, Hu Z Q.Chin J Nonferrous Met, 2000; 10(3): 301(宋洪伟,郭守仁,卢德忠,徐岩,王玉兰,胡壮麒.中国有色金属学报,2000;10(3):301) |
[23] | Stroup J P,Heacox R A.JOM,1969:46 |
[24] | Carreno F,Ruano O A.Acta Mater,1998;46(1):159 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%