在纯物质相场模型中,采用计算效率较高的邻界面点相场大梯度计算域控制法,模拟了纯金属在无量纲过冷度为0.55熔体中等轴枝晶的生长演化过程,得到与实验观察相符合的等轴枝晶生长规律,通过加入形式较简单的热扰动,产生了明显的二次枝晶臂,有的二次枝晶臂上还出现了三次枝晶臂.同时计算了枝晶晶轴尖端的无量纲生长速度和曲率半径,并求出Peclet数.计算结果与微观可求解理论和Ivantsov理论吻合良好.
参考文献
| [1] | Chen W C,Chien L C.J Synthetic Cryst,2002:31:245(陈万春,简来成.人工晶体学报.2002:31:245) |
| [2] | Wheeler A A, Murray B T, Schaefer R J. Physica, 1993:66D: 243 |
| [3] | Wang S L, Sekerka R F, Wheeler A A, Murray B T, Coriell S R, Rraun R J, McFadden G B. Physica, 1993: 69D: 189 |
| [4] | Warren J A, Boettinger W I. Acta Metal Mater, 1995: 43:689 |
| [5] | McCarthy J F. Acta Mater, 1997: 45:4077 |
| [6] | Wheeler A A, Boettinger W J, McFadden G B. Phys Rev,1992: 47E: 1893 |
| [7] | Kobayashi R. Physica, 1993: 63D: 410 |
| [8] | Karma A, Rappel W-J. Phys Rev, 1997: 57E: 4323 |
| [9] | Beckermann C, Diepers H J, Steinbach I, Karma A, Tong X. J Computat Phys, 1999: 154 |
| [10] | Karma A, Rappel W J. Phys Rev, 1999: 60E: 3614 |
| [11] | Provatas N, Goldendeld N, Jonathan D. Phys Rev Lett,1998: 80:3308 |
| [12] | Zhao D P, Jing T. Acta Metall Sin, 2002: 38:1238(赵代平,荆涛.金属学报,2002:12:1238) |
| [13] | Tong X, Beckermann C, Karma A. Weld Adv Solidific Processes. 1998:613 |
| [14] | Ivantsov G P, Dokl. Akada Nank USSR, 1974: 58:567 |
| [15] | Karma A, Rappel W J. Phys Rev, 1996: 53E: 3017 |
| [16] | Glicksman. Metal Mater Sci Eng, 1984: 65:45 |
| [17] | Hu H Q. Principle of Metal Solidification. Beijing: Machinery Press, 2000:127(胡汉起.金属凝固原理.北京:机械工业出版社.2000:127) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%