对强磁场作用下Bi-Mn合金分别从全熔态和从固液两相区开始的凝固过程及其组织的实验研究表明,磁场使初生MnBi相在试样外侧呈环状偏聚,其自身生长为棒状,棒的长轴沿磁场方向呈定向规则排列,而试样心部基本无初生MnBi相.在Curie点以上开始进行较慢的凝固时,由片状聚合而成的棒状MnBi具有单晶特征.对以上现象的形成原因进行了分析.
参考文献
| [1] | Farrell D E, Chandrasekhar B S, DeGuire M R, Fang M M, Kogan V G, Clem J R, Finnemore D K. Phys Rev,1987: 36B: 4025 |
| [2] | Rango P D, Lee M, Lejay P, Sulpice A, Tournier R, Ingold M, Germi P, Pernet M. Nature, 1991: 349:770 |
| [3] | Katsuki A, Tokunaga R, Watanabe S I. Chem Lett, 1996:(8): 607 |
| [4] | Sassa K, Morikawa H, Asai S. J Jpn Inst Met, 1997: 61:1283(佐佐健介,森川拓,浅井滋生日本金属学会志,1997:61:1283) |
| [5] | Wang H,Ren Z M,Deng K.Acta Matall Sin,200:38:41(王晖,任忠鸣,邓康.金属学报,2002:38:41) |
| [6] | Sassa K, Asai S. CAMP-ISIJ, 1998: 11:888 |
| [7] | Ren Z M, Su H, Jin J Z. Acta Matall Sin, 1990: 26:B374(任忠鸣,苏辉,金俊泽.金属学报1990:26:B374) |
| [8] | Moffatt W G. The Handbook of Binary Phase Diagrams.USA: Genium, 1984:11/83 |
| [9] | Feng D, Ding S Y, Zhai H R. Physics of Metal. Vol.4.Beijing: Science Press, 1998:460(冯端,丁世英,翟宏如金属物理学.第4卷,北京:科学出版社,1998:460) |
| [10] | Glew J P, Wong M K, Parker M R, Birss R R. IEEE Trans Mag, 1982: MAG-18:1656 |
| [11] | Wan D F, Luo S H. Physics of Magnetism. Beijing: Electronic Industry Press, 1987:8(宛德福,罗世华磁性物理.北京:电子工业出版社,1987:8) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%