对加压氰化浸出过程Pt族金属(Pt,Pd,Rh)行为的研究表明,Pt族金属氰化浸出率的顺序为Pd＞Pt＞Rh,而相应氰配合物高温下稳定性顺序为Rh≈Pt＞Pd.浸出过程中的行为规律实际上反映的是表面态Pt族金属的化学反应活性顺序,也即金属的原子态稳定性和金属键强度两种变化规律的综合表现.而Pt族金属氰配合物高温稳定性可以由"重Pt族配合物比相应结构的轻Pt族配合物的热力学稳定性更大,动力学惰性更高"以及金属氰配离子反应活性得到解释.
参考文献
| [1] | Mclnnes M F, Sparrow G J, Woodcock J T. Hydrometallurgy, 1993: (31): 157 |
| [2] | Atkinson G B, Kuczynski R J, Desmond D P. US Patent No.5160711, 1992 |
| [3] | Desmond D P. High-temperature Cyanide Leaching of Platinum Group Metals from Automobile CatalystsLaboratory Test. RI-9384, United States: Bureau of Mines, 1991. |
| [4] | Kuczynski R J. High-temperature Cyanide Leaching of Platinum Group Metals from Automobile CatalystsProcess Development Unit. RI-9428, United States: Bureau of Mines, 1992 |
| [5] | Chen J. Proceeding of 2002 China Peak Symposium of Precious Metals. Beijing Antaike Information Corp Lts.Shanghai: China Nonferrous Metal Industrial Information Center, 2002:15(陈景.2002年中国贵金属高峰研讨会会议论文集.上海:北京安泰科信息开发有限公司,2002:15) |
| [6] | Chen J. Huang K. Chinese Patent No. 01130222.4, 2001 |
| [7] | Chen J. Chin J Nonferrous Met, 2001: 11(2): 286(陈景.中国有色金属学报,2001:11(2):286-293) |
| [8] | Chen J. Chin Eng Sci, 2000: 2(7): 66(陈景.中国工程科学2000:2(7):66) |
| [9] | Chen J. The PGM Chemical Metallurgy Theory and Practice. Kunming: Yunnan Sci ＆ Tech Press, 1995: 1, 42.7(陈景.Pt族金属化学冶金理论与实践.昆明:云南科学技术出版社,1995:1,42.7 |
| [10] | Hancock R D. Inorg Chem, 1976: 15(4): 995 |
| [11] | Chen J. Chin Eng Sci, 1999: 1(2): 34(陈景.中国工程科学,1999:1(2):34) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%