研究了10%预应变Ti44Ni47Nb9合金应变约束相变加热温度Th对随后自由相变行为的影响,结果表明:经过约束相变循环的Ti44Ni47Nb9合金,在随后的自由相变过程输出两段恢复应变εr1和εr2,其值分别随约束相变加热温度Th升高而增加和减小,但合金总恢复应变εr(εr=εr1+εr2)却随Th升高而降低.分析表明:恢复应变εr1的降低与约束逆相变过程中马氏体相在恢复力作用下拉伸变形导致合金产生了大量塑性变形有关,而两段恢复应变εr1和εr2的形成则与合金约束相变后形成应变量明显不同的M1和M2两部分取向马氏体逆相变相关.
参考文献
| [1] | Metlon K N, Simpson J, Duerig T W. Proc Int Conf on Martensitic Trans, 1986:1053 |
| [2] | Melton K N, Proft J L, Duerig T W. Prog MRS Int Meeting on Advance Mater, 1988; 9:165 |
| [3] | Zhao L C, Duerig T W, Justi S, Melton K N, Proft J L,Yu W, Wayman C M. Scr Metall Mater, 1990; 24:221 |
| [4] | Cai W, Zhang C S, Zhao L C. J Mater Sci Technol, 1994;10: 27 |
| [5] | Madagopal K, Ganesh R Krishnan, Banerjee S. Scr Metall, 1988; 22:1593 |
| [6] | Brinson L C. J Intell Mater Syst Struct, 1993; 4:229 |
| [7] | Wen Y H, Li N, Tu M J. Scr Mater, 2001; 44:1113 |
| [8] | Piao M, Otsuka K, Miyazaki S, Horikawa H. Mater Trans JIM, 1993; 34:919 |
| [9] | Lin H C, Wu S K. Acta Metall Mater, 1994; 42:1623 |
| [10] | Liu X P, Jin W, Cao M Z, Yang D Z, Chen F X. Acta Metall Sin, 2002; 38:193(刘晓鹏,金伟,曹名洲,杨大智,陈騑騢.金属学报,2002;38:193) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%