用相场方法对二维晶粒长大过程进行仿真、结果表明,相场仿真所得准稳态晶粒尺寸分布,既可以用Weibull函数又可以用Louat函数很好地拟合,原因是在一定条件下两种分布函数的图像完全重合或非常相似.相场方法得到的晶粒拓扑分布经过演变同样达到了自相似或准稳态,但表现为对数正态分布形式.晶粒尺寸与晶粒边数间呈非线性关联.结果既与已有高纯度铝带实验结果相吻合,又与已有Monte Carlo法仿真结果一致.
参考文献
| [1] | Fayad W, Thompson C V, Frost H J. Scr Mater, 1999;40(10): 1199 |
| [2] | Wang C, Liu G Q, Qin X G. Acta Metall Sin, 2003; 39:635(王超,刘国权,秦湘阁.金属学报,2003;39:635) |
| [3] | Wang C, Liu G Q, Qin X G. ISIJ Int, 2003; 43(5): 774 |
| [4] | Fan D N, Chen L Q. Acta Mater, 1997; 45:611 |
| [5] | Fan D N, G Chengwei, Chen L Q. Acta Mater, 1997; 45:1115 |
| [6] | Anderson M P, Fortes M A. Philos Mag, 1989; B59:293 |
| [7] | Wang C. PhD Dissertation, University of Science and Technology Beijing. 2003.5(王超.北京科技大学博士学位论文,2003) |
| [8] | Nordbakke M W, Ryum N, Hunderi O. Acta Mater, 2002;50:3661 |
| [9] | Beck P A. Philos Mag Suppl, 1954; 3:245 |
| [10] | Tikare V, Holm E A, Fan D, Chen L Q. Acta Mater, 1999;47:363 |
| [11] | Mullins W W. Acta Mater, 1998; 46:6219 |
| [12] | Fradkov V E, Frachenko A S, Shvindlerman L S. Scr Met,1985; 19:1291 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%