为了能够从微观尺度上准确的描述凝固过程中枝晶生长情况,采用连续性模型使界面区域内的物理性质不连续现象变成连续型过渡,此外在界面区域内用平均溶质浓度来保证溶质守恒.模拟结果表明这种方法能够很好的处理固/液两相物理性质的差异,显示凝固过程中枝晶的生长、界面失稳、二次枝晶臂、三次枝晶臂的演化和显微偏析.
参考文献
[1] | Dilthey U, Pavlik K. In: Thomas B G, Beckermann C eds,Welding and Advanced Solidification Processes-Ⅷ. PA,Warrendale: 1998:589 |
[2] | Nastac L. Acta Mater, 1999; 47:4253 |
[3] | Zhu M F, Kim J M, Hong C P. ISIJ Inter, 2001; 41:992 |
[4] | Cho S H, Okane T, Umeda T. Sci Technol Adv Mater,2001; 2:241 |
[5] | Cinca G R. Physica A, 2002; 314:284 |
[6] | Nestler B, Wheeler A A, Garcke H. Comput Mater Sci,2003; 26:111 |
[7] | Damir J, Gretar T. J Comput Phys, 1996; 123:127 |
[8] | Udaykumar H S, Mao L. Int J Heat Mass Trans, 2002;45:4793 |
[9] | Eck C, Knabner P, Korotov S. J Comput Phys, 2002; 178:58 |
[10] | Li Q, Guo Q Y, Li D Z, Qian B N, Li D M, Li R, Zhang P W. Chin Phys Lett, 2004; 21:143 |
[11] | Kurz W, Giovanola B, Trivedi R. Acta Metall, 1986; 34:823 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%