对Fe-Ni-Nb-Ti-C合金在850℃变形后的等温弛豫过程中位错组态的演变以及应变诱导析出过程进行了TEM观察分析.样品的应力弛豫曲线可以明显地区分为三个阶段,分别对应应变诱导析出的孕育、形核长大和粗化过程.变形过程中产生的高密度、相互缠结的位错在等温弛豫过程中密度降低,并逐渐形成胞状结构.应变诱导析出在离散位错与胞界的位错网络上均能形核,但离散位错上颗粒析出密度更大.析出对位错产生的钉扎作用减缓了位错组态演变的进程.一旦析出颗粒发生粗化,则其钉扎作用减弱,而位错则以绕过机制摆脱析出颗粒的钉扎.
参考文献
| [1] | Yoshitaka A. In: Enomoto M ed., New Structure Steels and New Design of Constructions, 6th Workshop on the Ultra-steel, Tsukuba: The Iron and Steel Institute of Japan, 2002:91 |
| [2] | Adachi Y, Tomida T, Hinotani S. ISIJ, 2003, 40:S194 |
| [3] | Rainforth W M, Black M P, Higginson R L, Palmiere E J. Acta Mater, 2002, 50:735 |
| [4] | Lai Z H. Crystal Defects and Mechanical Properties of Metals, Beijing: Metallurgy Industry Press, 1988:294(赖祖涵.金属的晶体缺陷与力学性能,北京:冶金工业出版社,1988: 294) |
| [5] | Yang S W, Shang C J, Wang X M, He X L. J Univ Sci Technol Beijing, 2001, 3:214 |
| [6] | Yang S W, He X L, Chen M Z, Dang Z J, Ke J. Mater Sci Eng, 1994, 2:49(杨善武,贺信莱,陈梦谪,党紫九,柯俊.材料科学与工程,1994, 2: 49) |
| [7] | Feng D. Physics of Metals, Vol.1, Beijing: Science Press,2000:266(冯端.金属物理学,第一卷,北京:科学出版社,2000:266) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%