通过冷变形拉拔结合中间热处理,制备了纤维相增强的Cu-12Ag(质量分数,%)合金,采用不同温度退火研究了合金导电性能和抗拉强度随显微组织变化的关系.合金双相纤维复合组织在200℃热处理时无明显变化,强度略有降低,硬度和导电性能略有升高;当热处理温度超过400℃时,纤维组织演变为晶粒沿变形方向排列的等轴组织,合金强度及硬度显著下降,电导率显著上升.在热处理过程中,如果再结晶晶粒仅局限于原纤维组织内部生长而使得整体组织仍能保持完整的纤维形态,则合金能够表现出良好的强度与导电性匹配.
参考文献
| [1] | Hong S I, Hill M A, Sakai Y, Wood J T, Embury J D.Acta Metall Mater, 1995, 43:3313 |
| [2] | Frings P H, Bockstal L V. Physica B, 1995, 211:73 |
| [3] | Grunberger W, Heilmaier M, Schultz L. Physica B, 2001:643 |
| [4] | Sakai Y, Schneider-Muntau H J. Acta Mater, 1997, 45:1017 |
| [5] | Zhang Lei, Meng Liang. Mater Sci Technol, 2003, 19(1):75 |
| [6] | Ohsaki S, Yamazaki, Hono K. Scr Mater, 2003, 1569 |
| [7] | Benghalem A, Morris D G. Acta Mater, 1997, 45:397 |
| [8] | Han K, Embury J D, Sims J R, Campbell L J, SchneiderMuntau H J, Pantsyrnyi V I, Shikov A, Nikulin A, Vorobieva A. Mater Sci Eng, 1999, A267:99 |
| [9] | Sakai Y, Inoue Y, Maeda H. Acta Metall Mater, 1995, 43:1517 |
| [10] | Kwon H J, Hong S I. J Alloy Compds, 2001, 327:161 |
| [11] | Hong S I, Hill M A. Acta Mater, 1998, 46:4111 |
| [12] | Hong S I, Hill M A. Mater Sci Eng, 1999, A264:151 |
| [13] | Han K, Vasquez A A, Xin Y, Kalu P N. Acta Mater, 2003,51:767 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%