在Gleeble 1500热模拟机上对低碳钢Q235进行了热压缩实验,用电子探针分析了热变形试样微观组织中的碳浓度分布.结果表明,形变诱导铁素体晶粒中的碳含量明显过饱和.这表明在形变诱导铁素体相变过程中,碳没有发生明显的从铁素体向奥氏体扩散.从热力学的角度分析,在高于奥氏体-铁素体平衡转变温度Ae3变形,变形存储能的作用最终降低了体系相变后的自由能,使得在形变诱导铁素体相变过程中,碳无需发生从铁素体向奥氏体的扩散.
参考文献
| [1] | Yang Z M, Wang R Z. ISIJ Int, 2003: 43:761 |
| [2] | Priestner R, Hodgson P D. Mater Sci Technol, 1992: 8:849 |
| [3] | Huang Y D, Yang W Y, Sun Z Q. J Mater Proc Technol,2003: 134:19 |
| [4] | Hickson M R, Gibbs R K, Hodgson P D. ISIJ Int, 1999:39:1176 |
| [5] | Hodgson P D, Hickson M R, Gibbs R K. Scr Mater, 1999:40:1179 |
| [6] | Hurley P J, Hodgson P D, Muddle B C. Scr Mater, 1999:40:433 |
| [7] | Hodgson P D, Hickson M R, Gibbs R K. Mater Sci Forum,1998: 284:63 |
| [8] | Choo W Y, Kor J. Inst Met Mater, 1998: 36:1966 |
| [9] | Hong S C, Lim S H, Lee K J, Shin D H, Lee K S. ISIJ Int, 2003: 43:394 |
| [10] | Hong S C, Lee K S. Mater Sci Eng, 2002: A323:148 |
| [11] | Li C M, Yada H, Yamagata H. ISIJ Int, 1999: 39:209 |
| [12] | Yang W Y, Qi J J, Sun Z Q, Yang P. Acta Metall Sin,2004: 40:135(杨王玥,齐俊杰,孙祖庆,杨平.金属学报,2004:40:135) |
| [13] | Yang Z M,Zhao Y,Wang R Z,Ma Y W,Che Y M.Acta Metall Sin,2000:36:818(杨忠民,赵燕,王瑞珍,马燕文,车彦民.金属学报,2000:36:818) |
| [14] | Yang Z M,Zhao Y,Wang R Z,Ma Y W,Che Y M,Chen Q A.Acta Metall Sin,2000:36:1061(杨忠民,赵燕,王瑞珍,马燕文,车彦民,陈其安.金属学报,2000:36:1061) |
| [15] | Yada H, Li C M, Yamagata H. ISIJ Int, 2000: 40:200 |
| [16] | Matsumura Y, Yada H. Trans Iron Steel Inst Jpn, 1987:27:492 |
| [17] | Li C M, Yada H, Yamagata H. Scr Mater , 1998: 39:963 |
| [18] | TongM M, NiJ, ZhangYT, LiD Z, LiYY. Scr Mater,2004: 50:909 |
| [19] | Li J J. Mod Sci Instrum, 1997: (1): 54(李家驹.现代科学仪器,1997:(1):54) |
| [20] | Mao Y J.Metall Anal,2003:23:59(毛允静.冶金分析,2003:23:59) |
| [21] | Weng Y Q. ISIJ Int, 2003: 43:1675 |
| [22] | Peczak P, Luton M J. Acta Metall Mater, 1993: 41:59 |
| [23] | Yang P, Fu Y Y, Cui F E, Sun Z Q. Acta Metall Sin, 2001:37:601(场平,傅云义,崔凤娥,孙祖庆.金属学报,2001:37:601) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%