将经不同条件处理后的Cr5Mo+A302异种焊接接头放入NACE(TM-01-77)+H2S标准溶液中进行不同时间的腐蚀性研究,在扫描电镜(SEM)下逐次原位跟踪观察熔合区同一部位经不同腐蚀时间后的变化过程.研究结果表明:(1)与其它特征区相比,熔合区的耐腐蚀性能最差,产生"氢致剥离开裂";(2)经过焊后热处理的熔合区的抗腐蚀性进一步降低;(3)宽熔合区具有较强的抗"剥离开裂"腐蚀能力.上述现象与熔合区组织不均匀、碳迁移、氢富集和应力集中等因素有关.
参考文献
| [1] | Huang H H, Lee J T, Tsai W T. Mater Chem Phys, 1999;58:177 |
| [2] | Dong P, Zhang J. Eng Fracture Mech, 1999; 64:485 |
| [3] | Li G F, Charles E A, Conleton J. Corros Sci, 2001; 43:1963 |
| [4] | Guo H, Cai X, Yang W. Mater Mech Eng, 2002; 26(4): 1(郭浩,蔡洵,杨武.机械工程材料,2002;26(4):1) |
| [5] | Liu L W,Hu Q,Guo F,Zhao X Q,Wu J J.Corros Prot,2002;23(1):10(刘烈炜,胡倩,郭枫,赵新强,吴建军.腐蚀与防护,2002;23(1):10) |
| [6] | Zhang X C,Gong J M,Tu S D,Ling X.Pet Refinery Eng,2003;33(10):25(张显程,巩建鸣,涂善东,凌详.炼油技术与工程,2003;33(10):25) |
| [7] | Li Y T,Du Z Y,Tao Y Y,Xiong L Y.Trans Chin Weld Inst,2003;24(3):76(李云涛,杜则裕,陶勇寅,熊林玉.焊接学报,2003;24(3):76) |
| [8] | Pan C X. Dissimilar Steel and Dissimilar Metal WeldingMicrostructural Characterization and Transformation Behavior. Beijing: People's Communication Press, 2000:36(潘春旭.异种金属焊接-显微结构特征及其转变机理.北京:人民交通出版社,2000:36) |
| [9] | Lundin C D. Weld J, 1982; 61(2): 58-s |
| [10] | Faber G, Gooch T G. Welding World, 1982; 20(5/6): 87 |
| [11] | Li Z Y. Gorros Prot, 1977; 14(1): 51(李祖贻.石油化工腐蚀与防护,1997;14(1):51) |
| [12] | NACE Standard TM 0177, National Association of Corrosion Engineers, Houston, TX, 1990 |
| [13] | Xu J, Zhong M Y, Guo S X, Hardie D. J Chin Soc Corros Prot, 2003; 23(3): 149(徐坚,钟曼英,郭士行,Hardie D.中国腐蚀与防护学报,2003;23(3):149) |
| [14] | Yu G,Zhang X Y,Ke K.Petrochera Corros Prot,1999;16(4):51(余刚,张学元,柯克.石油化工腐蚀与防护,1999;16(4):51) |
| [15] | Morishige N, Kume R, Okabayashi H. Trans Jpn Weld Soc, 1985; 16(1): 12 |
| [16] | Kinoshita K, Ito H, Ebata A, Hattori T. Trans ISIJ, 1985;25:505 |
| [17] | Brouwer R C. Int d Pres Ves Piping, 1993; 56:133 |
| [18] | Pan C, Zhang Z. Mater Charact, 1994; 33(2): 87 |
| [19] | Li Y S, Niu Y, Wu W T. Corros Sci Prot Technol, 2000;12:41(李远士,牛焱,吴维(屮又).腐蚀科学与防护技术,2000;12:41) |
| [20] | Liu P. PhD Dissertation, Knoxville, USA: The University of Tennessee, 2001 |
| [21] | Pan C, Li A, Sun G, Holmquist M. Mater Sci Technol,1998; 14(3): 201 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%