系统地研究了Fe72.5Ga27.5合金不同冷却方式和制备工艺条件下的相结构和磁致伸缩性能.结果表明:该合金铸态、定向凝固态、快速凝固态和1000℃淬火时均保持D03结构.炉冷退火状态合金为D03和L12两相结构.炉冷时合金的饱和磁化强度达到140 A·m2/kg,淬火、定向凝固和快速凝固后,饱和磁化强度略低.快速凝固法制得的带材饱和磁场约为160 kA/m,远小于其它状态试样的饱和场强.退火态试样的室温饱和磁致应变为-59×10-6,铸态和定向凝固态均为53×10-6.淬火态合金的室温饱和磁致应变达到114×10-6.不同制备条件下合金的室温饱和磁致应变与其不同相结构密切相关.
参考文献
| [1] | Guruswamy S, Srisukhumbowornchai N, Clark A E,Restorff J B, Wun-Forgle M. Scr Mater, 2000; 43:239 |
| [2] | Clark A E, Wun-Forgle M, Restorff J B, Lograsso T A,Cullen J R. IEEE Trans Mag, 2001; 37:2678 |
| [3] | R Wu. J Appl Phys, 2002; 91:7358 |
| [4] | Srisukhumbowornchai N, Guruswamy S. J Appl Phys,2002; 92:5371 |
| [5] | Lograsso T A, Ross A R, Schlagel D L, Clark A E, WunForgle M. J Alloy Compd, 2003; 350:95 |
| [6] | Liu G D, Liu L B, Liu Z H, Zhang M, Chen J L, Li J Q,Wu G H, Li Y X, Qu J P, Chin T S. Appl Phys Lett, 2004;84:2124 |
| [7] | Kawamiya N, Adachi K, Nakamura Y. J Phys Soc Jpn,1972; 33:1318 |
| [8] | Clark A E, Wun-Forgle M, Restorff J B, Lograsso T A,Cullen J R. Proc 8th Joint Intermag Conf, San Antonio,TX, 2001 |
| [9] | Clerk A E, Hathaway K B, Wun-Fogle M, Restorff J B,Lograsso T A, Keppens V M, Petculescu G, Taylor R A.J Appl Phys, 2003; 93:8621 |
| [10] | Jiang C B, Liang T, Xu H B, Zhang M, Wu G H. Appl Phys Lett, 2002; 81:2818 |
| [11] | Ikeda O, Kainuma R, Ohnuma I, Fukamichi K, Ishida K.J Alloy Compd, 2002; 347:198 |
| [12] | KSster W, Godecke T. Z Metallkd, 1977; 68:661 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%