使用纯Ti粉和纯Ag块压制紧密接触的Ag-Ti二元扩散偶,在980,1100和1200℃下分别进行退火处理.通过金相观察和电子探针微区分析,对退火处理后的试样进行相分析和成分测定,从而获得了相应温度下的Ag-Ti二元体系的相平衡关系和共轭平衡成分.特别是针对液相、β(Ti)相和(TiAg)中间相,将实验所得的结果与文献报道的评估数据进行了比较.
参考文献
| [1] | Wallbaum H J. Naturwissenschaften, 1943; 31:91 |
| [2] | Raub E, Walter P, Engel M. Z Metallkd, 1952; 43:112 |
| [3] | van Thype R J, Rostoker W, Kessler H D. J Met, 1953;3:670 |
| [4] | Adenstedt H K, Freeman W. WADC Technol Rep, Part 11953:53 |
| [5] | McQuillan M K. J Inst Met, 1960; 88: 235. |
| [6] | Eremenko V N, Buyanov Y I, Panchenko N M. Porosh Metall, 1969; 79:55 |
| [7] | Plichta M R, Aaronson H I. Acta Metall, 1978; 26:1293 |
| [8] | Zhang Q Y, Zhuang H S. Handbook of Welding. Beijing:China Machine Presss, 1998:38(张启运,庄鸿寿.钎焊手册.北京:机械工业出版社,1998:38) |
| [9] | Pan W, Li R T, Chen J, Sun R F, Lian J. Mater Sci Eng,2000; 287: 72 |
| [10] | Cui P. J Hefei Univ Technol, 2002; 25:365(崔鹏.合肥工业大学学报,2002;25:365) |
| [11] | Yang X M. Semicond Optoelect, 2002; 23:274(杨雪梅.半导体光电,2002;23:274) |
| [12] | Murray J L, Bhansali K J. Bull Alloy Phase Diagram,1983; 4:178 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%