采用扫描电镜(SEM)、能谱分析(EDS)、X射线衍射(XRD)和电子探针(EPMA)对Fe3Al/Q235扩散焊界面的析出相形貌进行观察和成分测定,研究微观析出相的形成以及工艺参数(T,t,p)的影响.结果表明,Fe3Al/Q235扩散焊界面靠近Fe3Al一侧形成FeAl(Cr)析出相,是引起扩散焊接头脆性断裂的关键.扩散焊温度T、保温时间t与析出相区宽度y符合抛物线规律:y2=3.5(t-t0)exp[-5.6×104/(RT)].在降低加热温度和保温时间的条件下,增加焊接压力可促进Fe3Al/Q235界面原子的扩散,避免脆性析出相的形成,保证Fe3Al/Q235扩散焊接头的性能.
参考文献
| [1] | Fair G H , Wood J V. J Mater Sci, 1994; 29:1935 |
| [2] | Ma G, Xia Y M. Acta Metall Sin, 2002; 38:914(马钢,夏源明.金属学报,2002;38:914) |
| [3] | Mckamey C G, Maziasz P J, Jones J W. J Mater Res,1992; 7:2089 |
| [4] | Sun Z Q, Gao D C, Yang W Y, Huang X X, Huang J H.Chin J Mater Res, 2001; 15:69(孙祖庆,高德春,杨王玥,黄晓旭,黄继华.材料研究学报,2001;15:69) |
| [5] | David S A, Zacharia T. Weld J, 1993; 72:201 |
| [6] | Gao D C, Yang W Y, Dong M, Huang J H, Sun Z Q. Acta Metall Sin, 2000; 36:87(高德春,杨王玥,董敏,黄继华,孙祖庆.金属学报,2000;36: 87) |
| [7] | Ni J S, Zhu J H, Wan X J, Xie B L. Welding, 1995; (1): 5(倪建森,朱家红,万晓军,谢蓓玲.焊接,1995;(1):5) |
| [8] | Li Y J, Wang J, Yin Y S, Wu H Q, Feng J C. Trans Chin Weld Inst, 2002; 23:25(李亚江,王娟,尹衍升,吴会强,冯吉才.焊接学报,2002;23: 25) |
| [9] | Li Y J, Wu H Q, Wang J. Mater Sci Technol, 2003; 19:227 |
| [10] | Li D Q, Lin D L. J Mater Eng, 1997; (3): 20(郦定强,林栋梁.材料工程,1997;(3):20) |
| [11] | Shi Y X, Zhang Y W. Trans Chin Weld Inst, 1985; 6:177(施雨湘,张有为.焊接学报,1985;6:177) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%