在无磁场的条件下,降温过程中Bi-Mn合金在340℃发生包晶相变,顺磁性Mn1.08Bi相转变为铁磁性MnBi相,同时伴随着相的形态变化,由块状转变成片状;在10 T磁场中,Mn1.08Bi相发生包晶相变的温度升高至介于360-370℃之间,且MnBi相晶体发生了分裂,分裂后的小晶体沿磁场方向定向排列和聚合.从磁场诱发应变的角度分析了磁场对相变温度和MnBi相形态的影响.
参考文献
| [1] | de Rango P,Lee M,Lejay P,Sulpice A,Tournier B,Ingold M,Germi P,Pemet M.Nature,1991; 349:770 |
| [2] | Braithwaite D,Beaugnon E.Nature,1991; 354(14):134 |
| [3] | Farrel D E,B S.Phys Rev,1987; 36B:4025 |
| [4] | Tkaczyk J E,Lay K W.J Mater Res,1990; 5:1368 |
| [5] | Chen K,Maheswaran B,Liu Y P,Giessen B,Chang C,Markiewicz R.Appl Phys Lett,1989; 55:289 |
| [6] | Ostertag C P,Shull R D,Vauolin M D,Blendell J E,Stearns L C,Fuller E R.Ceramic Supercond Ⅱ,1988:232 |
| [7] | Guo X,Altounian Z,Olsen J O S.J Mater Res,1990; 5:2646 |
| [8] | Decarlo J L,Pirich R G.Metall Trans,1984; 15A:2155 |
| [9] | Shetty M N,Rawat D K,Rai K N.J Mater Sci,1987; 22:19089 |
| [10] | Yasuda H,Ohnaka I,Yamamoto Y.Mater Trans,2003,44:2207 |
| [11] | Sugiyama T,Tahashi M,Sassa K,Shigeo A.Mater Trans JIM,1998; 39:814 |
| [12] | Wang H,Ren Z M,Deng K.Acta Matall Sin,2002,38:41(王晖,任忠鸣,邓康.金属学报,2002,38:41) |
| [13] | Guo X,Altounian Z,Strom-Olsen J O.J Appl Phys,1991;69:6067 |
| [14] | Li X,Ren Z M.Chin J Nonferr Met,2005; 15:397(李喜,任忠鸣.中国有色金属学报,2005;15:397) |
| [15] | Moffatt W G.The Handbook of Binary Phase Diagrams.USA:Genium,1984 |
| [16] | Liu Y.PhD thesis.Shanghai Institute of Ceramis,The Chinese Academy of Sciences,2004(刘岩.中国科学院上海硅酸盐研究所博士学位论文,2004) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%