随着氢浓度增加,Ti-60合金中的初生α相的体积分数、(α+β)→β相变点及高温屈服强度均连续降低.高温拉伸时合金的最低屈服点出现在相应氢浓度下的(α+β)→β相变点处,进一步增加氢含量反而使合金的屈服强度升高,其原因是氢强化了β相.Ti-60合金中氢浓度w(H)与(α+β)→β相变点满足方程:t(α+β)→β(℃)=815+210exp(-3w(H)).900℃拉伸时,0.3%的氢使合金的屈服强度降幅达70%.
参考文献
| [1] | Han M C.Aerosp Mater Technol,1999; (1):23(韩明臣.宇航材料工艺,1999;(1):23) |
| [2] | Ilyin A A,Polkin I S,Moamonov A M,Nosov V K.In:Blenkinsop P A,Evans W J,Flower H M,eds.,Titanium'95:Science and Technology,London:Institute of Materials,1996:2462 |
| [3] | Costa J E,Williams T C,Thompson A W.Metall Trans,1987; 18A:1421 |
| [4] | Hou H L,Li Z Q,Wang Y J,Guan Q.Chin J Nonferrous Met,2003; 13:533(侯红亮,李志强,王亚军,关桥.中国有色金属学报,2003;13:533) |
| [5] | Senkov O N,Froes F H.Int J Energy,1999; 24:565 |
| [6] | Murzinova M A,Salishchev G A,Afonichev D D.Int J Energy,2002; 27:775 |
| [7] | Kerr W R,Smith P R,Rosenblum M E,Gurney F J,Mahajan Y R,Bidwell L R.In:Kimura H,Izumi O,eds.,Titanium 80:Science and Technology.Warrendale:TMSAIME,1980:2477 |
| [8] | Lai Z H.In:Sun W C,Cui Z P,eds.,Proc 7th National Conf on Titanium and Titanium Alloys,Changsha:Central South University of Technology Press,1991:266(赖祖涵.见:孙文川,崔祝屏主编,第七届全国钛及钛合金学术交流会文集,长沙:中南工业大学出版社,1991:266) |
| [9] | Fang T Y,Wang W H.Mater Chem Phys,1998; 56:35 |
| [10] | Yang K,Edmonds D V.Scr Metall Mater,1993; 28:71 |
| [11] | Senkov O N,Jonas J J.Metall Mater Trans,1996; 27A:1869 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%