强磁场可明显影响Al 4.5%Cu(质量分数)合金定向凝固组织.在温度梯度GT=38 K/cm,生长速率较低(R=5 μm/s)时,10 T强磁场使液-固界面处的树枝晶变得不规则,低于共晶温度以下的固相区定向枝晶组织消失,组织细化;在生长速率R=50 μm/s时,10 T强磁场使得枝晶沿与凝固方向成一定角度定向排列,X射线衍射表明〈111〉方向转向磁场方向;在生长速率较高(R=100μm/s)的情况下,10 T强磁场使得枝晶粗化,一次枝晶间距增大.从热电磁流体理论和磁晶的各向异性角度分析了上述现象.
参考文献
| [1] | Katsuki A,Tokunaga R,Watanabe S,Tanimoto Y.Chem Lett,1996; 25:607 |
| [2] | Tahashi M,Sassa K,Asai S.Mater Trans,2002; 43:2813 |
| [3] | Fang Q Q,Fang R Y,Zhang S,Dai D S.J Magn Magn Mater,1998; 188:241 |
| [4] | Shercliff J A.J Fluid Mech,1979; 91:231 |
| [5] | Lehmann P,Moreau R,Camel D,Bolcato R.Acta Mater,1998; 46:4067 |
| [6] | Boettinger W J,Biancaniello F S,Coriell S R.Metall Trans,1981; 12A:321 |
| [7] | Tewari S N,Shah R,Song H.Metall Mater Trans,1994;25A:1535 |
| [8] | Wu Q,Ren Z M,Li X,Deng K,Zhong Y B,Ma J P.Prog Nat Sci,2004; 14:830(吴琼,任忠鸣,李喜,邓康,钟云波,马娟萍.自然科学进展,2004;14:830) |
| [9] | Ma J P,Ren Z M,Deng K,Li X,Wu Q.Prog Nat Sci,2004; 14:837(马娟萍,任忠鸣,邓康,李喜,吴琼.自然科学进展,2004;14:837) |
| [10] | Callen H B.Phys Rev,1984; 73:1349 |
| [11] | Cui Z Q.Metallurgy and Heat Treatment.Beijing:China Machine Press,1994:10(崔忠圻.金属学与热处理.北京:机械工业出版社,1994:10) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%