采用原位反应喷射沉积法制备TiCp/7075半固态铝合金坯料,在600℃保温10-60 min,研究半固态二次加热过程中合金的晶粒长大规律,并与喷射沉积7075铝合金进行对比分析.结果表明,添加原位TiC颗粒后,合金的晶粒长大指数由2增加到3,晶粒长大速率明显减慢.其原因是添加TiC颗粒后合金晶粒长大激活能增加1倍左右,使得合金的晶粒长大更加困难,显示出原位TiC颗粒对喷射沉积7075铝合金的晶粒长大具有显著的抑制作用.
参考文献
| [1] | Kang Z T,Zhang H,Chen Z H.Chin J Nonferrous Met,1998; 8:595(康智涛,张豪,陈振华.中国有色金属学报,1998;8:595) |
| [2] | Yu F X,Cui J H,Ranganathan S,Dwarakadasa E S.Mater Sci Eng,2001; A304-306:261 |
| [3] | Jung H K,Kang C G.J Mater Proc Technol,2000; 104:244 |
| [4] | Annavarapu S,Doherty R D.Acta Metall Mater,1995;43:3207 |
| [5] | Lawrynowicz D E,Wolfenstine J,Lavernia E J.Mater Sci Eng,1997; A230:1 |
| [6] | Wang J L,Su Y H,Tsao C Y A.Scr Mater,1997; 37:2003 |
| [7] | MansonWhitton E D,Stone I C,Jones J R,Grant P S,Cantor B.Acta Mater,2002; 50:2517 |
| [8] | Yang B,Wang F,Huang Z J,Duan X J,Zhang J S.Mater Rev,2001; 15(3):4(杨滨,王锋,黄赞军,段先进,张济山.材料导报,2001;15(3):4) |
| [9] | Wu G,Yao L J,Li Z X,Peng R Q,Zhao Z D.Aluminum and Aluminum Alloys Handbook.Beijin:Science Press,1997:255(武恭,姚良均,李震霞,彭如清,赵祖德.铝及铝合金材料手册.北京:科学出版社,1997:255) |
| [10] | Lu G M,Dong J,Cui J Z .Chin J Nonferrous Met,2001;11:211(路贵民,董杰,崔建忠.中国有色金属学报,2001;11:211) |
| [11] | Lawrynowicz D E,Wolfenstine J,Lavernia E J .Mater Sci Eng,1997; A230:1 |
| [12] | Kawanishi S,Isonishi K,Okazaki K.Mater Trans,1993;34(1):49 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%