根据最大熔深时TiO2,Cr2O3,CdCl2和ZnCl2活性剂中元素在焊缝中的分布分析了熔池的流动情况,在此基础上对上述4种活性剂对镁合金交流TIG焊接熔深的影响进行了研究.结果表明,这4种活性剂均可增加焊缝熔深,活性剂的涂敷量均有一个饱和值.加大涂敷活性剂后不同程度的改变了熔池中Mg,Al元素的分布.涂敷CdCl2,ZnCl2后在焊缝中没有观察到活性剂元素,而涂敷TiO2,Cr2O3后在焊缝中观察到了Ti,Cr,O元素,氯化物活性剂增加熔深的机理主要是活性剂与电弧的相互作用,氧化物活性剂增加熔深的机理主要是活性剂与熔池金属的相互作用.
参考文献
| [1] | Leinonen J I,Karjalainen L P.In:David S A,Vitek J M eds,Proc 2nd Int Conf on Trends in Welding Research.Materials Park,USA:ASM International,1989:387 |
| [2] | Lucas W,Howse D.Weld Met Fabrica,1996; 64:11 |
| [3] | Gurevich S M,Zamkov V N,Kushirenko N A.Autom Weld,1965; 18:1 |
| [4] | Gurevich S M,Zamkov V N.Autom Weld,1966; 19:14 |
| [5] | Liu F Y,Yang C L,Lin S B,Wu L,Zhang Q T.Acta Metall Sin,2003; 39:661(刘凤尧,杨春利,林三宝,吴林,张清涛.金属学报,2003;39:661) |
| [6] | Niagaj J.Weld Int,2003; 17:257 |
| [7] | Pascal P,Jacques S.Mater Sci Forum,2003; 426-432:4087 |
| [8] | Bonnefois B,Coudreuse L,charles J.Weld Int,2004; 18:208 |
| [9] | Perry N,Marya S,Soutif E.In:Vitek J M,David S A,Johnson J A,Smartt H B,DebRoy Teds,Proc 5th Int Conf on Trends in Welding Research (ASM/AWS).Pine Mountain,Ga:ASM International,1998:520 |
| [10] | Middel W,Den Ouden G.In:Vitek J M,David S A,Johnson J A,Smartt H B,DebRoy Teds,Proc 5th Int Conf on Trends in Welding Research (ASM/AWS).Pine Mountain,Ga:ASM International,1998:394 |
| [11] | Marya M,Edwards G R.Weld J,2002; 81:291-S |
| [12] | Marya M.Weld World,2002; 46:7 |
| [13] | Zhang Z D,Liu L M,Shen Y,Wang L.Chin J Nonferr Met,2005; 15:912(张兆栋,刘黎明,沈勇,王来.中国有色金属学报,2005;15:912) |
| [14] | Zhang Z D,Liu L M,Wang L.Trans Chin Weld Inst,2004;25:55(张兆栋,刘黎明,王来.焊接学报,2004;25:55) |
| [15] | Toshikatsu A,Tokisue H.J Jpn Inst Light Met,1995;45:70(朝比奈敏胜,时末光.轻金属,1995;45:70) |
| [16] | Boddy P J,Utsumi T.J Appl Phys,1971; 42:3369 |
| [17] | Saha M N.Philos Mag,1920; 40:272 |
| [18] | Lu S P,Fujii H,Sugiyama H,Tanaka M,Nogi K.Mater Trans,2002; 43:2926 |
| [19] | Wark K.Thermodynamics.3rd ed,New York:McGraw-Hill,1977:833 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%