以Al-M(M=Sr,Nd)二元相图、Miedema生成热模型和Toop模型为基础,建立了Mg-Al-M三元合金熔体中Al-M金属间化合物析出行为的热力学计算模型,并采用该模型对Mg-8Al-3.5Sr熔体中Al-Sr金属间化合物的析出温度进行了计算,结果与文献基本吻合.利用该模型对一定温度下Mg-9/6Al-M(M=Sr,Nd)熔体中优先析出Al-M金属间化合物所需M的最低含量进行了计算.根据计算结果,对Al-M金属间化合物在Mg-9/6Al-M合金熔体中的析出行为以及对合金力学性能可能的影响进行了分析和比较,提出了采用稀土Nd和碱土Sr复合添加来制备耐热镁合金的思路.
参考文献
| [1] | Lu Y Z,Wang Q D,Zeng X Q,Ding W J,Zhai C Q,Zhu Y P.Mater Sci Eng,2000; A278:66 |
| [2] | Baril E,Labelle P,Pekguleryuz M O.JOM,2003; 55(11):A34 |
| [3] | Huang X F,Fu P H,Lu C,Ding W J.Chin J Mater Res,2004; 18:593(黄晓锋,付彭怀,卢晨,丁文江.材料研究学报,2004;18:593) |
| [4] | Chartrand P,Pelton A D.J Phase Equilib,1994; 15:590 |
| [5] | Parvez1 M A,Wang X,Essadiqi E,Medraj M.In:Neelameggham N R,Kaplan H I,Powell B R,eds.,Magnesium Technology 2005.Warrendale,USA,PA:TMS,2005:179 |
| [6] | Miedema A R,de Boer P F,de Chatel P F.Physica,1980;100B:1 |
| [7] | Dragan M,Dragana Z,Zivan Z.J Serb Chem Soc,2005;70:9 |
| [8] | Sheng J W,Yamana H,Moriyama H.Royal Soc Chem,2001; 14:1 |
| [9] | Chen X Q,Ding X Y,Liu X,Zheng H Y,Rogl P.J Northeast Univ (Nat Sci),2000; 21:270(陈星秋,丁学勇,刘新,郑海燕,Rogl P.东北大学学报(自然科学版),2000;21:270) |
| [10] | Fan P,Zhou G Z.Acta Metall Sin,1999;35:421(范鹏,周国治.金属学报,1999;35:421) |
| [11] | Massalski T B,Murray J L,Bennett L H.Binary Alloy Phase Diagrams.Cleveland,Ohio:American Society for Metals Press,1986:140 |
| [12] | Powell B R,Rezhets V M,Balogh M P,Waldo R A.JOM,2002; 54(8):34 |
| [13] | Anyanwu I A,Gokan Y,Nozawa S,Suzuki A,Kamado S,Kojima Y,Takeda S,Ishida T.Mater Trans,2003; 44:562 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%