以金属Ti为阳极,不锈钢薄片和镀Mo玻璃为阴极,采用恒电流电沉积的方法制备了化学计量比为1:1、厚度为1μm且致密均匀的Cu-In薄膜.分析了镀液离子浓度、电流密度、络合剂含量及添加剂种类对薄膜成分及形貌的影响.在除电流密度外其它工艺条件相同的情况下,采用不同阴极材料为衬底沉积Cu-In薄膜时,薄膜形貌、成分无差别,且电流密度对薄膜的形貌和成分控制起着关键的作用.此外,在镀液离子低浓度范围内,及Cu/In离子浓度比不变的前提下,镀液中金属离子总浓度的改变不会影响镀层的成分和形貌;十二烷基硫酸钠和苯亚磺酸钠可作为理想的辅助添加剂,能改善薄膜形貌,使其表面均匀、规整.由该方法制备的Cu-In预置膜可以进一步硒化得到理想的CuInSe2薄膜.
参考文献
| [1] | Bekker J,Alberts V,Witcomb M J.Thin Solid Films,2001; 387:40 |
| [2] | Powalla M,Dimmler B.Solar Energy Mater Solar Cells,2003; 75:27 |
| [3] | Wada T,Hashimoto Y,Nishiwaki S,Satoh T,Hayashi S,Negami T,Miyake H.Solar Energy Mater Solar Cells,2001; 67:305 |
| [4] | Yuksel O F,Baso B M,Safak H,Karabiyik H.Appl Phys,2001; 73A:387 |
| [5] | Kenji Y,Daisuke M,Tetsuo I.Appl Phys Lett,2000; 77:259 |
| [6] | Hagiwara Y,Nakada T,Kunioka A.Solar Energy Mater Solar Cells,2001; 67:267 |
| [7] | Wijesundera R P,Siripala W.Solar Energy Mater Solar Cells,2004; 81:147 |
| [8] | Nakamura S,Yamamoto A.Solar Energy Mater Solar Cells,2003; 75:81 |
| [9] | Ugarte R,Schrebler R,Córdova R,Dalchiele E A,Gómez H.Thin Solid Films,1999; 340:117 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%