采用实验-数值方法对40Cr和30CrMnSiNi2A两种高强钢三点弯曲试样在不同加载速率的冲击载荷作用下进行了动态断裂韧性的测试,并对其率相关性进行研究.实验在Hopkinson压杆系统上完成,试样的起裂时间采用应变片法测得.结合有限元三维动态模拟,得到了不同加载速率下试样动态应力强度因子的时间历程并由实测的起裂时间确定材料动态断裂韧性.结果表明,在本工作加载速率范围内(106 MPa·m1/2/s),40Cr钢为解理型断裂,其动态断裂韧性随加载速率增加的变化趋势不明显;而30CrMnSiNi2A钢则在较大程度上表现为延性断裂的特征,其动态断裂韧性随加载速率的增加呈明显上升趋势.并对上述结果进行了宏观和微观机理分析.
参考文献
| [1] | Fan T Y.Introduction To Dynamic Fracture Mechanics.Beijing:Beijing Institute of Technology Press,1990:51(范天佑.断裂动力学引论.北京:北京理工大学出版社,1990:51) |
| [2] | Zhao Y P.Adv Mech,1996; 26:362(赵亚溥.力学进展,1996; 26:362) |
| [3] | Liu R T,Zhang X X,Jiang F C,Ou G B.J Harbin Eng Univ,2000; 21:18(刘瑞堂,张晓欣,姜风春,欧贵宝.哈尔滨工程大学学报,2000; 21:18) |
| [4] | Zheng J,Wang Z P,Duan Z P.Adv Mech,1994; 24:459(郑 坚,王泽平,段祝平.力学进展,1994; 24:459) |
| [5] | Yu J L.Mech Eng,1992; 14:7(虞吉林.力学与实践,1992; 14:7) |
| [6] | Rokach I V.Fatigue Fract Eng Mater Struct,1998; 21:1007 |
| [7] | Nakano M,Kishida K.Eng Fract Mech,1990; 36:515 |
| [8] | Li Y L.Rare Met Mater Eng,1993; 22(5):12(李王龙.稀有金属材料与工程,1993; 22(5):12) |
| [9] | Li Y L,Guo W G,Jia D X,Liu Y Y.Acta Mech Solid Sin,1995; 8:210 |
| [10] | Li Y L,Liu Y Y.J Comput Struct Mech Appl,1995; 12(1):110(李玉龙,刘元镛.计算结构力学及应用,1995; 12(1):110) |
| [11] | Guo W G.,Li Y L,Liu Y Y.Theory Appl Fract Mech,1997; 26:29 |
| [12] | Ruiz C,Mines R A W.Int J Fract,1985; 29:101 |
| [13] | Li Y L,Liu Y Y.Theory and Test Research on Dynamic Fracture Toughness and Dynamic Crack Propagation.Xi'an:Northwest Polytechnical University Press,1995:108(李玉龙,刘元镛.动态起裂韧性及动态裂纹扩展的理论与实验研究.西安:西北工业大学出版社,1995:108) |
| [14] | Chen E P,Sih G C.In:Sih G C,ed.,Elastodynamic Cra ck Problems,Leyden:Noordhoff Publishing,1976:1 |
| [15] | Xu Z J,Li Y L,Liu Y Y,Luo J R,Chen Y Z.Acta M etall Sin,2006; 42:635(许泽建,李玉龙,刘元镛,罗景润,陈裕泽.金属学报,2006; 42:635) |
| [16] | Cui Y X,Wang C L.Metal Failure Surface Analysis.Ha erbin:Harbin Institute of Technology Press,1998:34(崔约贤,王长利.金属断口分析.哈尔滨:哈尔滨工业大学出版社,1998:34) |
| [17] | Zhang D,Zhong P D,Tao C H,Lei Z S.Failure Analysis.Beijing:National Defence Industry Press,1998:87(张 栋,钟培道,陶春虎,雷祖圣.失效分析.北京:国防工业出版社,2004:87) |
| [18] | Campbell J D,Ferguson W G.Philos Mag,1970; 21:63 |
| [19] | Wu Y S,Chen Y J,Zeng C H.Microcosmic Fracture Mechanics.Xi'an:603th Research Institute of Ministry of Aeronautic Industry,1987:254(伍义生,陈一坚,曾春华.微观断裂力学.西安:航空工业部第六零三研究所,1987:254) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%