采用真空电弧熔炼方法制备了不同Ta含量的Nb-Nb5Si3共晶合金,显微组织和压缩性能的研究表明:Ta主要固溶在Nb基体相中,随Ta含量的增加,Nb5Si3相逐渐减少;Ta促使β-Nb5Si3相转变为α-Nb5Si3相;Ta的加入有利于复合材料室温和高温强度的提高,Ta含量为5%(原子分数)的材料高温压缩强度最高.
参考文献
| [1] | Caron P,Khan T.Aerosp Sci Technol,1999; 3:513 |
| [2] | Fu H Z.J Aeronaut Mater,1998; 18(4):52(傅恒志.航空材料学报,1998;18(4):52) |
| [3] | Radhakrishnan R,Bhanduri S,Henager C H.JOM,1997;49(1):41 |
| [4] | Bewlay B P,Jackson M R,Zhao J C,Subramanian P R.Metall Mater Trans,2003; 34A:2043 |
| [5] | Qu S Y,Wang R M,Han Y F.Mater Rev,2002; 16(4):31(曲士昱,王荣明,韩雅芳.材料导报,2002;16(4):31) |
| [6] | Gao L M,Guo X P.Mater Rev,2005; 19(7):72(高丽梅,郭喜平.材料导报,2005;19(7):72) |
| [7] | Subramanian P R,Mendiratta M G,Dimiduk D M,Stucke M A.Mater Sci Eng,1997; A239-240:1 |
| [8] | Bewlay B P,Jackson M R,Lipsitt H A.Metall Mater Trans,1996; 27A:3801 |
| [9] | Kim W Y,Tanaka H,Kasama A.Intermetallics,2001; 9:521 |
| [10] | Kim J H,Tabaru T,Sakamoto M,Hanada S.Mater Sci Eng,2004; A372:137 |
| [11] | Qu S Y,Wang R M,Han Y F.J Aeronaut Mater,2001;21(3):9 (曲士昱,王荣明,韩雅芳.航空材料学报,2001;21(3):9) |
| [12] | Mendiratta M G,Lewandowski J J,Dimiduk D M.Metall Trans,1991; 22A:1573 |
| [13] | Menon E S K.In:Kim Y W,Carneiro Teds,Niobium:High Temperature Applications,Proc,Warrendale,USA:TMS,2003:63 |
| [14] | Kumar K S,Manna S K.Mater Res Soc Symp Proc,1989;133:415 |
| [15] | Massalski T B.Binary Alloy Phase Diagram.2nd,Materials Park,Ohio:The Materials Information Society,1996:2764 |
| [16] | Massalski T B.Binary Alloy Phase Diagram.2nd,Materials Park,Ohio:The Materials Information Society,1996:2772 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%