在不同温度下对Al-Cu合金试件进行固溶处理,以改变溶质原子在固溶体中的浓度及析出相在合金中的含量.对所得到的Al-Cu合金试件进行常应变率拉伸实验,观察其应力-时间关系曲线.由拉伸实验现象分析溶质原子及析出相对位错运动的影响,从而探究Portevin-Le Chatelier(PLC)效应产生的微观机制.结果表明,当固溶处理温度由500℃逐步降低,应力-时间曲线上的锯齿幅值逐渐减小,并在300℃时达到最小值;继续降低固溶处理温度至100℃,锯齿幅值又逐渐增大.固溶处理温度高于300℃时,溶质原子对PLC效应的影响强于析出相的影响而起主要作用;反之,固溶处理温度低于300℃时,析出相对PLC效应的影响强于溶质原子的影响而起主要作用.
参考文献
| [1] | Bell J F.Encyclopedia of Physics,Mechanics of Solids Ⅰ.Berlin:Springer-Verlag Press,1973:41,649 |
| [2] | Munz D,Macherauch E.Z Metallkd,1966; 57:552 |
| [3] | Mulford R A,Kocks U F.Acta Metall,1979; 27:1125 |
| [4] | Tian B H,Li H X,Zhang Y G,Chen C Q.Acta Metall Sin,1998; 34:603(田宝辉,李焕喜,张永刚,陈昌麒.金属学报,1998;34:603) |
| [5] | Jiang H F,Zhang Q C,Jiang Z Y,Wu X P.Acta Metall Sin,2005;41:727(江慧丰,张青川,蒋震宇,伍小平.金属学报,2005;41:727) |
| [6] | Chihab K,Estrin Y,Kubin L P.Scr Metall,1987; 21:203 |
| [7] | Jiang H F,Zhang Q C,Jiang Z Y,Chen Z J,Wu X P.Chin Phys Lett,2005; 22:99(江慧丰,张青川,蒋震宇,陈忠家,伍小平.中国物理快报,2005;22:99) |
| [8] | Pink E,Grinberg A.Mater Sci Eng,1981; A51:1 |
| [9] | McCormick P G.Trans Indian Inst Met,1986; 39:98 |
| [10] | Chihab K,Estrin Y,Kubin LP,Vergnol J.Scr Metall,1987; 21:203 |
| [11] | Jiang Z Y,Zhang Q C,Jiang H F,Chen Z J,Wu X P.Mater Sci Eng,2005; A403:154 |
| [12] | Cottrell A H.Dislocations and Plastic Flow in Crystals.London:Oxford University Press,1953:1 |
| [13] | Wang C,Xu Y B,Han E H.Acta Metall Sin,2006; 42:191(王聪,徐永波,韩恩厚.金属学报,2006;42:191) |
| [14] | McCormick P G.Acta Metall,1972; 20:351 |
| [15] | Estrin Y,Kubin L P.In:Mühlhaus H B,ed.,Continum Models for Materials With Microstructures,New York:John Wiley & Sons Ltd.,1995:395 |
| [16] | Rizzi E,Hahner P.Int J Plast,2004; 20:121 |
| [17] | Picu R C.Acta Mater,2004; 52:3447 |
| [18] | Picu R C,Vincze G,Ozturk F,Gracio J J,Barlat F,Maniatty A M.Mater Sci Eng,2005; A390:334 |
| [19] | Chen Z J,Zhang Q C,Jiang Z Y,Jiang H F,Wu X P.J Mater Sci Technol,2004; 20:535 |
| [20] | Jiang H F,Zhang Q C,Xu Y H,Wu X P.Acta Metall Sin,2006; 42:139(江慧丰,张青川,徐毅豪,伍小平.金属学报,2006;42:139) |
| [21] | Jiang H F,Zhang Q C,Xu Y H,Wu X P.Acta Phys Sin,2006; 55:409(江慧丰,张青川,徐毅豪,伍小平.物理学报,2006;55:409) |
| [22] | Lu J Y,Jiang Z Y,Zhang Q C.Acta Metall Sin,2006; 42:6(卢俊勇,蒋震宇,张青川.金属学报,2006;42:6) |
| [23] | Zhang S L,Ren S Z.Concise Manual of Aluminum Alloy.Shanghai:Shanghai Scientific and Technological Literature Press,2001:11(张士林,任颂赞.简明铝合金手册.上海:上海科学技术文献出版社,2001:11) |
| [24] | Zhang Q C,Jiang Z Y,Jiang H F,Chen Z J,Wu X P.Int J Plast,2005; 21:2150 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%