利用分析电子显微镜(AEM)研究了在用化学气相沉积方法沉积SiC过程中加入游离碳对SiC纤维(W芯)微结构的影响.游离碳能够有效的避免在SiC/W芯界面上出现WO3,排除氧元素在纤维中存留;同时还能够有效地抑制W芯附近SiC晶粒的长大,并在SiC中形成许多同心的富C层.这些微结构上的变化可使SiC纤维强度从2800 MPa提高到3600 MPa.
参考文献
| [1] | Dicarlo J A.J Met,1985;37(6):44 |
| [2] | Hooker J A,Doorbar P J.Mater Sci Technol,2000;16:725 |
| [3] | Guo Z X,Derby B.Prog Mater Sci,1995;39:411 |
| [4] | Wang S Y,Zhang R G.Fibers Reinforced Composites,Shanghai:Donghua University Press,1998(王善元,张汝光.纤维增强复合材料,上海:东华大学出版社,1998) |
| [5] | Leyen C,Hausmann J,Kumpfert J.Adv Eng Mater,2003;5:399 |
| [6] | Cheng T T,Jones I P,Shatwell R A,Doorbar P.Mater Sci Eng,1999;A260:139 |
| [7] | Wawner F W,Teng A Y,Nutt S R.SAMPE Q,1983;14(3):39 |
| [8] | Ning X J,Pirouz P.J Mater Res,1991;6(10):2234 |
| [9] | Shinozaki S S,Sato H.J Am Ceram Soc,1978;61:425 |
| [10] | Keyse R J,Garratt-Reed A J,Goodhew P J,Lorimer G W.Introduction to Scanning Transmission Electron Microscopy,Singapore:Springer,1998 |
| [11] | Guo C Y,Zhang C B,He L L,Jin B H,Shi N L.J Mater Sci Technol,accepted |
| [12] | Smith P R,Froes F H.J Met,1984;(March):19 |
| [13] | Fred G,Rainer S F.Mater Sci Eng,1995;B34:224 |
| [14] | Deng J,Luo G Z,Ding W Z.Rare Met Mater Eng,1991;20(6):10(邓炬,罗国珍,丁文周.稀有金属材料与工程,1991;20(6):10) |
| [15] | Dyos K,Shatwell R A.J Microsc,1999;196:175 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%