通过分析连铸结晶器振动过程参数和结晶器内摩擦力,确定了一种新的非正弦振动形式下1.8和2.0 m/min拉速时的非正弦振动因子,并阐明了非正弦振动因子随拉速提高的变化规律.结果表明:1.8和2.0 m/min拉速时非正弦振动因子适宜值为0.2,与实际应用值一致;振动频率和振幅不变,拉速由2.0 m/min升至2.2 m/min,非正弦振动因子应增至0.25,以改善振动效果.
参考文献
| [1] | Mikio S,Hideaki M,Toru K,Kiminari K,Shigetaka U,Yoshimi K.ISIJ Int.1991:31:254 |
| [2] | Meng X N,Zhu M Y.Chin J Process Eng,2006;6(Suppl.):91(孟祥宁,朱苗勇.过程工程学报,2006;6(增刊):91) |
| [3] | Kwon O D,Choi J,Lee I R,Kim J W,Moon K H,Shin Y K.74th Steelmaking Con,Proc,1991:561 |
| [4] | Wang H F,Shen G Q.Shanghai Met,2004;26(1):37(汪洪峰,沈国强.上海金属,2004;26(1):37) |
| [5] | Li X K,Zhu Q X,Zheng X R,Zhang D M.Iron Steel,1998;33(11):26(李宪奎,朱清香,郑学然,张德明.钢铁,1998;33(11):26) |
| [6] | Gan Y,Chen D L,Yang W G.Iron Steel,1999;34(4):16(干勇,陈栋梁,杨文改.钢铁,1999;34(4):16) |
| [7] | Yao M,Wang W H,Wei S L,Yin H B,Fang D C.J Dalian Univ Technol,2002;42:195(姚曼,王文华,魏树立,尹合壁,方大成.大连理工大学学报,2002;42:195) |
| [8] | Li X K,Zhang D M.Continuous Casting Mold Oscillation Technology.Beijing:Metallurgical Industry Press,2000:30(李宪奎,张德明.连铸结晶器振动技术.北京:冶金工业出版社,2000:30) |
| [9] | Zhang H B,Wang H Z.Iron Steel,1995;30(11):17(张洪波,王海之.钢铁,1995;30(11):17) |
| [10] | Wang Z L,Guo S B,Wang G L,Shi Z X.Iron Steel,2005;40(1):31(王子亮,郭世宝,王广林,石中雪.钢铁,2005;40(1):31) |
| [11] | Thomas B G,Li G,Moitra A,Habing D.80th Steelmaking Conf Proc,1997:183 |
| [12] | Akira Y,Toshihiko E,Seshadri S.ISIJ Int,2002;42:1084 |
| [13] | Joong K P,Indira V S,Brian G T,Yoon U.83th Steelmaking Conf Proc,2000:9 |
| [14] | Thomas B G.ISIJ Int,1995;35:737 |
| [15] | Zhang Y W,Zhu L G,Ding W Z.J Iron Steel Res,2002;14(4):21(张玉文,朱立光,丁伟中.钢铁研究学报,2002;14(4):21) |
| [16] | Zhu L G,Wang S M,Jin S T.J Univ Sci Technol Beijing,1999;21(1):13(朱立光,王硕明,金山同.北京科技大学学报,1999;21(1):131 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%