采用Mishin镶嵌原子势,通过分子动力学方法模拟了非晶Cu在压痕作用下的形变诱导晶化行为,考察了压痕过程中能量、应力与微观结构演化的关系.局部塑性变形区域出现微小晶核,随着变形的增加,晶核不断生长与合并,局部塑性变形是导致非晶晶化的根本原因最终生成的晶粒具有面心立方结构,其(111)密排面平行于剪切面.非晶相中的纳米晶粒能提高非晶材料的刚度.
参考文献
| [1] | Greer A L.Science,1995; 267:1947 |
| [2] | Schneider S.J Phys:Condense Matter,2001; 13:7723 |
| [3] | Lu K.Acta Metall Sin,1994; 30:B1(卢柯.金属学报,1994;30:B1) |
| [4] | Ogura M,Tarumi R,Shimojo M,Takashima K,Higo Y.Appl Phys Lett,2001; 79:1042 |
| [5] | Chen H,He Y,Shiflet G J,Poon S J.Nature,1994; 367:541 |
| [6] | Kim J J,Choi Y,Suresh S,Argon A S.Science,2002; 295:654 |
| [7] | Lee J C,Kim Y C,Ahn J P,Kim H S,Lee S H,Lee B J.Acta Mater,2004; 52:1525 |
| [8] | Mishin Y,Mehl M J,Papaconstantopoulos D A,Voter A F,Kress J D.Phys Rev,2001; 63B:224106 |
| [9] | Daw M S,Baskes M I.Phys Rev,1984,29B:6443 |
| [10] | Daw M S,Baskes M I.Phys Rev Lett,1983; 50:1285 |
| [11] | Ackland G J,Tichy G,Vitek V,Finnis M W.Philos Mag,1987; 56A:735 |
| [12] | Lee H J.Molecular Dynamics Studies of Metallic Glass.Pasadena:California Institute of Technology,2003 |
| [13] | Honeycutt J D,Andersen H C.J Phys Chem,1987; 91:4950 |
| [14] | Nose S.Mol Phys,1984; 52:255 |
| [15] | Parrinello M,Rahman A.J Appl Phys,1981; 52:7182 |
| [16] | Lilleodden E T,Zimmerman J A,Folies S M,Nix W D.J Mech Phys Solids,2003; 51:901 |
| [17] | Schuh C A,Nieh T G.Acta Mater,2003; 51:87 |
| [18] | Ogura A,Tarumi R,Shimojo M,Takashima K,Higo Y.Appl Phys Lett,2001; 79:1042 |
| [19] | Tarumi R,Ogura A,Shimojo M,Takashima K,Higo Y.Jpn J Appl Phys,2000; 39:L611 |
| [20] | Sutton M,Yang Y S,Mainville J,Jordan-Sweet J L,Ludwig K F,Stephenson G B Jr.Phys Rev Lett,1989; 62:288 |
| [21] | Lu K,Wang J T.Acta Metall Sin,1990; 26:B316(卢柯,王景唐.金属学报,1990;26:B316) |
| [22] | Lu K,Wang J T,Dong Lin.Acta Metall Sin,1991; 27:B31(卢柯,王景唐,董林.金属学报,1991;27:B31) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%