研究了导电聚合物聚苯胺(PAni)/聚苯乙烯(PS)微/纳米复合材料的电磁波吸收特性.随掺杂态PAni在复合材料中的含量增加,复合材料电导率和PAni/PS复合板的吸波能力随之提高.PAni的微观形貌对吸波性能有影响,纤维形貌PAni要比颗粒形貌PAni具有更好的吸波特性.经过优化后,厚度为1.80 mm的掺杂态PAni/PS微/纳米复合材料雷达波反射率小于10 dB的频宽达6 GHz(11.6-17.6 GHz).
参考文献
| [1] | Psilopoulos J,Gruber J.Microwave Opt Technol Lett,2001; 30:254 |
| [2] | Zhao J P,Li Y,Wu P L.Mater Sci Technol,2002; 10:219(赵九蓬,李垚,吴佩莲.材料科学与工艺,2002;10:219) |
| [3] | Heeger A J.Rev Mod Phys,2001; 73:681 |
| [4] | Olmedo L,Hourquebie P,Jousse F.Synth Met,1995; 65:205 |
| [5] | Wan M X,Li J C,Li S Z.Polym Adv Technol,2001; 12:651 |
| [6] | Vinoy K J,Jha R M.Sādhanā,1995; 20:815 |
| [7] | Xing L Y.Stealing Materials.Beijing:Chemical Industry Press,2004:82(邢丽英.隐身材料.北京:化学工业出版社,2004:82) |
| [8] | Courric S,Tran V H.J Polym Adv Technol,2000; 11:273 |
| [9] | Wan M X,Li S Z,Li J C,Chao Y.Aerosp Mater Technol,1989; (4):28(万梅香,李素珍,李军朝,曹镛.宇航工艺材料,1989;(4):28) |
| [10] | Liao H X,Liu Z L,Yu G X.J Cent Chin Norm Univ (Nat Sci),2004; 38:340(廖海星,刘祖黎,喻古雄.华中师范大学学报(自然科学版),2004;38:340) |
| [11] | Coltevieille D,Le Méhauté A,Challioui C,Mirebeau P,Demay J N.Synth Met,1999; 101:703 |
| [12] | Ge F D,Zhu J,Chen L M.Aerosp Mater Technol,1996;(5):42(葛副鼎,朱静,陈利民.宇航材料工艺,1996;(5):42) |
| [13] | Guo X M.PhD Dissertation,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2005(郭雪梅.中国科学院金属研究所博士学位论文,沈阳,2005) |
| [14] | Kang Q.Novel Microwave Absorbing Materials.Beijing:Science Press,2005:66(康青.新型微波吸收材料.北京:科学出版社,2005:66) |
| [15] | Zou Y,Wang G Q,Liao H X,Liu Z L.J Huazhong Univ Sci Technol (Nat Sci),2001; 29:87(邹勇,王国强,廖海星,刘祖黎.华中科技大学学报,2001;29:87) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%