通过对均匀化退火后的AZ91镁合金热挤压以及随后的时效处理,分析了形变及时效过程对材料组织与性能的影响.结果表明:AZ91镁合金在320和380 ℃挤压时发生了动态再结晶,组织比铸态细化,力学性能大幅度提高;随后的时效处理进一步提高了挤压镁合金的力学性能.经380℃挤压及200℃,10 h的时效处理后,其抗拉强度σb可达357 MPa,延伸率δ达到8%.
参考文献
[1] | Mordike B L,Ebert T.Mater Sci Eng,2001; A302:37 |
[2] | Friedrich H,Schumann S.J Mater Process Technol,2001;117:276 |
[3] | Matucha K H.In:Cahn R W,Hassen P,Kramer E J,eds.; translated by Ding D Y,et al.,Materials Science and Technology:A Comprehensive Treatment,Vol.8:Structure and Properties of Nonferrous Alloys,Beijing:Science Press,1999:105(Matucha K H.见:Cahn R W,Hassen P,Kramer E J,主编;丁道云,等,译.材料科学与技术丛书,第8卷:非铁合金的结构和性能,北京:科学出版社,1999:105) |
[4] | Watanabe H,Tsutsui H,Mukai T,Kohzu M,Tanabe S,Higashi K.Int J Plast,2001; 17:387 |
[5] | Aghion E,Bronfin B,Eliezer D.J Mater Process Technol,2001; 117:381 |
[6] | Kleiner S,Beffort O,Wahlen A,Uggowitzer P J.J Light Met,2002; 2:277 |
[7] | Cizek L,Greger M,Pawlica L,Dobrzanski L A,Tanski T.J Mater Process Technol,2004; 157-158:466 |
[8] | Liu Z,Liu C Y,Wang Z G,Wang Y,Han X L.Acta Metall Sin,1999; 35:869(刘正,刘重阳,王中光,王越,韩行林.金属学报,1999;35:869) |
[9] | Mabuchi M,Kubota K,Higashi K.Mater Trans JIM,1995; 36:1249 |
[10] | Yu BY,Bao C L,Song H W,Qiao R J,Liu Z,Yu H P.Hot Work Technol,2005; 34(8):30(于宝义,包春玲,宋鸿武,乔日金,刘正,于海朋.热加工工艺,2005;34(8):30) |
[11] | Jin J B,Wang Z X,Liu X F,Xie J X.Acta Metall Sin,2006; 42:1014(金军兵,王智祥,刘雪峰,谢建新.金属学报,2006;42:1014) |
[12] | Ion S E,Humphreys F J,White S H.Acta Metall,1982;30:1909 |
[13] | Mao W M,Zhao X B.Recrystallization and Grain Growth of Metals.Beijing:Metallurgical Industry Press,1994:47(毛卫民,赵新兵.金属的再结晶与晶粒长大.北京:冶金工业出版社,1994:47) |
[14] | Duly D,Simon J P,Brechet Y.Acta Metall Mater,1995;43:101 |
[15] | Celotto S.Acta Mater,2000; 48:1775 |
[16] | Kubota K,Mabuchi M,Higashi K.J Mater Sci,1999; 34:2255 |
[17] | Wang L Y,Huang G S,Fan Y G,Huang G J.Chin J Nonferrous Met,2003; 13:594(汪凌云,黄光胜,范水革,黄光杰.中国有色金属学报,2003;13:594) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%