用基于密度泛函理论的自洽离散变分方法研究了bcc Fe中[100](010)刃型位错扭折处掺S的电子结构,计算了杂质偏聚能、原子间相互作用能、电荷密度及态密度.计算结果表明:S引入体系后,电荷发生了重新分布,S原子得到电子,其周围Fe原子失去电子,且S原子的3p轨道与近邻Fe原子的3d4s4p轨道之间杂化,使得它们之间的成键有较强的方向性,可影响材料的韧性;而近邻Fe原子因失去电子使自身之间相互作用比未掺杂时减弱,有利于扭折的迁移,可能影响材料的强度.
参考文献
| [1] | Yan J A,Wang C Y,Duan W H,Wang S Y.Phys Rev,2004; 59B:214110 |
| [2] | Niu Y,Zhao D L,Wang C Y.Acta Metall Sin,2001; 37:239(牛原,赵栋梁,王崇愚.金属学报,2001;37:239) |
| [3] | Feng Y Q,Wang C Y.J Alloy Compd,2000; 312:219 |
| [4] | Alexander H.In:Nabarro F R N ed.,Dislocation in Solids.Amsterdam:North-Holland,1986:115 |
| [5] | Gornostyrev Y N,Katsnelson M I,Stroev A Y,Trefilov A V.Phys Rev,2005; 71B:094105 |
| [6] | Wen M,Fukuyama S,Yokogawa K.Acta Mater,2003; 51:1767 |
| [7] | Chen L Q,Qiu Z C,Wang C Y,Yu T.J Alloy Compd,2007; 428:49. |
| [8] | Chen L Q,Qiu Z C.Defect Diffus Forum,2007; 261:37 |
| [9] | Ellis D E,Benesh G A,Byrom E.Phys Rev,1977; 16B:3308 |
| [10] | Guenzburger D,Ellis D E.Phys Rev,1992; 45B:285 |
| [11] | Barth U Von,Hedin L.J Phys C:Solid State Phys,1972;5:1615 |
| [12] | Chen L Q,Wang C Y,Yu T.Acta Phys Sin,2006; 55:5980(陈丽群,王崇愚,于涛.物理学报,2006;55:5980) |
| [13] | Chen L Q,Wang C Y,Yu Tao.J Appl Phys,2006; 100:023715 |
| [14] | Delley B.J Chem Phys,1990; 92:508 |
| [15] | Delley B.J Chem Phys,1991; 94:7245 |
| [16] | Wang C Y,Zhao D L.Mater Res Soc Symp Proc,1994;318:571 |
| [17] | Wang C Y.Acta Metall Sin,1997; 33:54(王崇愚.金属学报,1997;33:54) |
| [18] | Mulliken R S.J Chem Phys,1955; 23:1833 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%