在把网格引入的各向异性的影响降低到合理范围的基础上,采用相场法研究了在无弹性场作用时,沉淀颗粒间的扩散场相互作用对沉淀相形貌及成分的影响.模拟结果表明:由于扩散场的相互作用,在沉淀相生长及粗化过程中,沉淀颗粒形貌可出现圆形→方形→圆形→菱形→圆形的多种变化,且沉淀内部呈现成分不均匀性.随着沉淀相体积分数的增大,沉淀颗粒间的扩散场相互作用加强,对沉淀相形貌及其成分的影响也更加显著.
参考文献
| [1] | Wang Y Z,Chen L Q,Khachaturyan A G.Scr Metall Mater,1991; 25:1387 |
| [2] | Wang Y Z,Chen L Q,Khachaturyan A G.Phys Rev,1992;46B:11194 |
| [3] | Wang Y Z,Khachaturyan A G.Acta Metall Mater,1995;43:1837 |
| [4] | Wang Y Z,Chen L Q,Khachaturyan A G.Scr Metall Mater,1991; 25:1969 |
| [5] | Wang Y Z,Khachaturyan A G.Philos Mag,1995; 72A:1161 |
| [6] | Hu S Y,Chen L Q.Acta Mater,2001; 49:1879 |
| [7] | Hou H,Zhao Y H,Chen Z,Xu H.Acta Metall Sin,2005;41:695(侯华,赵宇宏,陈铮,徐宏.金属学报,2005;41:695) |
| [8] | Li X L,Chen Z,Liu X G,Liu B.Acta Metall Sin,2002;38:458(李晓玲,陈铮,刘晓光,刘兵.金属学报,2002;38:458) |
| [9] | Braun R J,Cahn J W,McFadden G B,Wheeler A A.Philos Trans R Soc London,1997; 355A:1787 |
| [10] | Wang Y Z,Banerjee D,Su C C,Khachaturyan A G.Acta Mater,1998; 46:2983 |
| [11] | Li D Y,Chen L Q.Scr Mater,1997; 37:1271 |
| [12] | Vaithyanathan V,Chen L Q.Acta Mater,2002; 50:4061 |
| [13] | Wang J C,Osawa M,Yokokawa T,Harada H,Enomoto M.Comput Mater Sci,2007; 39:871 |
| [14] | Zhu J Z,Chen L Q,Shen J,Tikare V.Phys Rev,1999;60E:3564 |
| [15] | Chen L Q,Shen J.Comput Phys Commun,1998; 108:147 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%