采用非平衡磁控溅射沉积技术在SCM415渗碳淬火钢基片上沉积了无氢Ti掺杂类金刚石(Ti-DLC)薄膜和无氢高纯类金刚石(DLC)薄膜,通过调节Ti靶的溅射功率使获得的Ti-DLC薄膜Ti含量(原子分数)为1.9%-34%.利用Raman分光光谱仪、XPS,XRD、显微硬度计及纳米划痕仪分析研究了Ti-DLC的组织结构、显微硬度及薄膜附着力.结果表明,利用非平衡磁控溅射得到的Ti-DLC薄膜,在Ti含量小于25%时,Ti-DLC薄膜仍具有类金刚石薄膜的sp2,sp3结构,但Ti的掺杂促进了sp3键向sp2键的转变.掺杂的Ti以TiC纳米晶的形式存在于非晶态的DLC中.掺杂Ti后薄膜的硬度明显降低,而薄膜附着力明显改善;但是当Ti含量超过3%后,薄膜附着力无明显变化,硬度逐渐回升.
参考文献
| [1] | Yang S,Li X,Renevier N M,Teer D G.Surf Coat Technol,2001; 142/144:85 |
| [2] | Narayan R J.Appl Surf Sci,2005; 247:217 |
| [3] | Weng K W,Chen Y C,Lin T N,Wang D Y.Thin Solid Films,2006; 515:932 |
| [4] | Kulikovsky V,Bohac P,Franc F,Deineka A,Vorlicek V,Jastrabik L.Diamond Relat Mater,2001; 10:1076 |
| [5] | Fu Y H,Zhu X D,He J W,Yang S C.Tribology,2003; 23:463;(付永辉,朱晓东,何家文,Yong S C.摩擦学报,2003;23:463) |
| [6] | Siegal M P,Barbour J C,Provencio P N,Tallant D R,Friedmann T A.Appl Phys Lett,1998; 73:759 |
| [7] | Siegal M P,Tallant D R,Provencio P N,Provencio D L,Overmyer D L,Simpson R L,Martine-Miranda L J.Appl Phys Lett,2000; 76:3052 |
| [8] | Saitoh H.J Surf Finish Soc Jpn,2002; 53:706;(斋藤秀俊.表面技术,2002;53:706) |
| [9] | Rusli,Yoon S F,Yang H,Ahn J,Huang Q F,Zhang Q,Guo Y P,Yang C Y,Teo E J,Wee A T S,Huan A C H.Thin Solid Films,1999; 355/356:174 |
| [10] | Strondl C,Carvalho N M,de Hosson J Th M,van der Kolk G J.Surf Coat Technol,2003; 162:288 |
| [11] | Yang B,Huang Z H,Gao H T,Fan X J,Fu D J.Surf Coat Technol,2007; 201:6808 |
| [12] | Veprek S,Haussmann M,Reiprich S.Mater Res Soc Symp Proc,1996; 86/87:394 |
| [13] | MouraeSilva C W,Branco J R T,Cavaleiro A.Thin Solid Films,2006; 515:1063 |
| [14] | Pal S K,Jiang J C,Efstathios I.Meletis Surf Coat Technol,2007; 201:7917 |
| [15] | Baba K,Hatada R,Tanaka Y.Surf Coat Technol,2007;201:8362 |
| [16] | Dekempeneer E,Van Acker K,Vercammen K,Meneve J,Neerinck D,Eufinger S,Pappaert W,Sercu M,Smeets J.Surf Coat Technol,2001; 142-144:669 |
| [17] | Robertson J.Prog Solid State Chem,1991; 21:199 |
| [18] | Hu Y W,Li L H,Cai X,Chen Q L,Chu P K,Diamond Relat Mater,2007; 16:181 |
| [19] | Wang P,Wang X,Xu T,Liu W M,Zhang J Y.Thin Solid Films,2007; 515:6899 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%