建立了3种物理模型,研究了纳米复合永磁材料中晶粒尺寸、两相分布及体积分数与矫顽力间的变化关系.计算结果表明:不同的两相分布导致晶粒接触界面分数变化,从而引起晶间交换耦合作用的涨落;相分布影响纳米复合永磁体矫顽力的大小,但没有改变其随晶粒尺寸变化的关系;设计理想的相分布并且适当控制晶粒尺寸.是实现纳米复合永磁材料高矫顽力的可能途径.
参考文献
| [1] | Manaf A,Buckley R A,Davies H A,Leonowicz M.J Magn Magn Mater,1991; 101:360 |
| [2] | Betancourt J I,Davies R H A.J Magn Magn Mater,2002;246:6 |
| [3] | Billona O V,Urreta S E,Fabietti L M,Bertorello H R.J Magn Magn Mater,1998; 187:371 |
| [4] | Feng W C,Gao R W,Yah S S,Li W,Zhu M G.J Appl Phys,2005; 98:044305 |
| [5] | Fukunaga H,Kuma J,Kanai Y.IEEE Trans Magn,1999;35:3235 |
| [6] | Sun X K,Zhang J,Chu Y L,Liu W,Cui B Z,Zhang Z D.Appl Phys Left,1999; 74:1740 |
| [7] | Bauer J,Seager M,Zero A,Kronmiiller H.J Appl Phys,1996; 80:1667 |
| [8] | Xiao Q F,Zhao T,Zhang Z D.J Magn Magn Mater,2001;223:215 |
| [9] | Liu W,Zhang Z D,Liu J P,Chen L J,He L H,Liu Y,Sun X K,Sellmyer D J.Adv Mater,2002; 14:1832 |
| [10] | Liu W,Zhang Z D,Liu J P,Dai Z R,Wang Z L,Sun X K,Sellmyer D J.J Phys,2003; 36D:63 |
| [11] | Skomski R,Coey J M D.IEEE Trans Magn,1993; 29:2860 |
| [12] | Arcas J,Hernando A,Barandiaran J M.Phys Rev,1998;58B:5193 |
| [13] | Chena Z M,Wu Y Q,Kramerb M J,Smith B R,Ma B M,Huang M Q.J Magn Magn Mater,2004; 268:105 |
| [14] | Melsheimer A,Seeger M,Kronmüller H.J Magn Magn Mater,1999; 202:458 |
| [15] | Kronmiiller H,Fischer R,Seeger M,Zern A.J Phys,1996;29D:2274 |
| [16] | Kneller E F,Hawig R.IEEE Trans Magn,1991; 27:3588 |
| [17] | Feng W C,Gao R W,Han G B,Zhu M G,Li W.Acts Phys Sin,2004; 53:3171(冯维存,高汝伟,韩广兵,朱明刚,李卫.物理学报,2004;53:3171) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%