利用金相、电子背散射衍射(EBSD)技术结合纳米压痕仪研究了低碳Mn-Mo-Nb-B微合金钢的组织转变、晶粒的晶体学取向及其纳米力学性能.由1℃/s冷速连续冷却到室温所得组织主要是贝氏体铁素体和粒状贝氏体.以1℃/s冷速连续冷却到560℃淬水所得组织为针状铁素体和淬水时形成的马氏体/贝氏体,其中相邻针状铁索体之间为小角晶界;前一试样中粒状贝氏体的平均纳米压痕硬度(2.31 GPa)与后一试样中针状铁素体的平均纳米压痕硬度(2.22 GPa)极为接近.取向差较小的针状铁素体组织在1℃/s冷速下连续冷却过程中碰撞,接合成粒状贝氏体.
参考文献
| [1] | ISIJ.Atlas for Bainitic Microstructures (Vol.1),Tokyo:ISIJ,1992 |
| [2] | Krauss G,Thomposon T W.ISIJ Int,1995; 35:937 |
| [3] | Ohtani H,Okaguchi S,FujishroY,Ohmori Y.Metall Trans,1990; 21A:877 |
| [4] | Shang C J,Hu L J,Yang S W,Wang X M,Zhao Y T,He X L.Acta Metall Sin,2005; 41:471(尚成嘉,胡良均,杨善武,王学敏,赵运堂,贺信莱.金属学报,2005;41:471) |
| [5] | Zhao Y T,Shang C J,He X L,Guo H.Acta Metall Sin,2006; 42:54(赵运堂,尚成嘉,贺信莱,郭晖.金属学报,2006;42:54) |
| [6] | Zhao Y T,Shang C J,Yang S W,Wang X M,He X L.Mater Sci Eng,2006; A433:169 |
| [7] | Mangonon P L.Merall Trans,1976; 9A:1389 |
| [8] | Bhadeshia H K D H,Svensson L E,Gretoft B.Acta Metall,1985; 33:1271 |
| [9] | Bhadeshia H K D H,Svensson L E.J Mater Sci,1989; 24:3180 |
| [10] | Ali A,Bhadeshia H K D H.Mater Sci Technol,1991; 7:895 |
| [11] | Thompson S W,Colvin D J,Krass G.Metall Trans,1990; 21A:1493 |
| [12] | Habraken L J.Proc 4th Inter Conf on Electron Microscopy.Berlin:Springer-Verlag,1958:621 |
| [13] | Suh D W,Kang J H,Oh K H,Lee H C.Scr Mater,2003; 48:91 |
| [14] | Chio Y,Choo W Y,Kwon D.Scr Mater,2001; 45:1401 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%