借助于光学显微镜研究了磁场强度对Fe-0.76%C合金冷却转变过程的先共析铁素体显微组织的影响.结果表明:随着磁场强度的增强,该合金的先共析铁素体析出量和共析点的含碳量均明显增加.原因可归结为,强磁场使Fe-C合金的共析点向高温及高含碳量区域移动,使奥氏体向铁素体转变的初始温度升高.强磁场使先共析铁素体沿磁场方向伸长,而且随着磁场强度的增加,先共析铁素体的伸长方向与磁场方向之间夹角的平均值逐渐减小.上述现象可解释为:外加磁场使先共析铁素体晶核成为磁偶极子,并使其周围奥氏体原子作为磁偶极子更易于沿磁场方向向铁素体晶核扩散.
参考文献
| [1] | Pustovoit V N,Dombrovskii Y M,Grishin S A.Met Sci Heat Treat,1979;21:838 |
| [2] | Shimotomai M,Maruta KI Mine K,Matsui M.Acta Mater,2003;51:2921 |
| [3] | Maruta K,Shimotomai M.Mater Trans JIM,2000;41:902 |
| [4] | Shimotomai M,Maruta K I.Scr Mater,2000;42:499 |
| [5] | Hao X J,Ohtsuka H.J Mater Metall,2005;4:132 (Hao X J,Ohtsuka H.材料与冶金学报,2005;4:132) |
| [6] | Hao X J,Ohtsuka H.CAMP-ISIJ,2004;17:1229 (Hao X J,Ohtsuka H.日本铁钢协会讲演论文集,2004;17:1229) |
| [7] | Jaramillo R A,Babu S S,Ludtka G M,Kisner R A,Wilgen J B,Mackiewicz-Ludtka G,Nicholson D M,Kelly S M,Murugananth M,Bhadeshia H K D H.Scr Mater,2005;52:461 |
| [8] | Kakeshita T,Shimizu K,Funada S,Date M.Acta Metall,1985;33:1381 |
| [9] | Choi J-K,Ohtsuka H,Xu Y,Choo W-Y.Scr Mater,2000;43:221 |
| [10] | Joo H D,KimS U,Shin N S,Koo Y M.Mater Lett,2000;43:225 |
| [11] | Guo H,Enomoto M.Mater Trans JIM,2000;41:911 |
| [12] | ZhangY D,He C S,Zhao X,Zuo L,Esling C.Solid State Phenom,2005;105:187 |
| [13] | Zhang Y D,He C S,Zhao X,Zuo L,Esling C.J Magn Magn Mater,2004;284:287 |
| [14] | ZhangY D,Esling C,Muller J,He C S,Zhao X,Zuo L.Appl Phys Lett,2005;87:212504 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%