利用带有正四棱锥形金刚石压头的Vickers显微硬度计对0Cr18Ni10Ti不锈钢焊接接头的焊缝、母材,熔合区及热影响区的压痕尺寸效应进行了研究,实验载荷为0.098-4.9 N,载荷保持时间均为10 S.结果表明,接头各区域的显微硬度在较小的载荷下随实验载荷的增加而减小,当载荷超过1.96 N时各区域硬度值基本保持恒定.采用PSR模型对接头各区域硬度值随载荷的变化规律进行了较为准确的描述,得到的HVPSR与1.96 N载荷下的实验结果间的误差小于3%.在2.94 N的实验载荷下沿垂直接头方向连续进行了微压痕测试,得到接头在不同位置处的显微硬度分布曲线,并对接头的金相组织进行了观察和分析.
参考文献
| [1] | Xu Z J,Li Y L,Liu M S,Li P Z,Wu Y G.Acta Metall Sin,2008;44:98 (许泽建,李玉龙,刘明爽,李朋洲,吴云刚.金属学报,2008;44:98) |
| [2] | Ade F.Weld J,1991;70:53 |
| [3] | Grough I G.Met Forum,1988;12:31 |
| [4] | Chen T H,Yang J R.Mater Sci Eng,2002;A338:166 |
| [5] | Zou M L,Zou Y X,Du C X,Sun D C,Chen H M.Foundation of Welding Theory and Technology.Beijing:Beijing University of Aeronautics & Astronautics Press,1994:168 (邹茉莲,邹一心,杜诚修,孙德超,陈焕明.焊接理论及工艺基础.北京:北京航空航天大学出版社,1994:168) |
| [6] | Bamzai K K,Kotru P N,Wanklyn B M.Appl Surf Sci,1998;133:195 |
| [7] | Sahin O,Uzun O,Kolemen U,Ucar N.Mater Charact,2007;58:197 |
| [8] | Gong J H,Miao H Z,Zhao Z,Guan Z.Mater Sci Eng,2001:A303:179 |
| [9] | Xu Z J,Li Y L.Acta Metall Sin (Engl Lett),in press |
| [10] | Ascheron C,Haase C,Kuhn G,Neumann H.Cryst Res Technol,1989;24:K33 |
| [11] | Kick F.Das Gesetz der Proportionalen Widerstanden und Seine Anwendung,Leipzig:Felix,1885 |
| [12] | Bamzai K K,Kotru P N,Wanklyn B M.Cryst Res Technol,1996;31:813 |
| [13] | Kumari P N S,Kalainathan S,Raj N A N.Mater Lett,2008;62:305 |
| [14] | Vangatesan B,Kanniah N,Ramaswamy P.J Mater Sci Lett,1986;5:987 |
| [15] | Bhatt V P,Patel R M,Desai C F.Cryst Res Technol,1983;18:9 |
| [16] | Dhar P R,Bamzai K,Kotru P N.Cryst Res Technol,1997;32:535 |
| [17] | Li H,Bradt R C.J Mater Sci,1993;28:917 |
| [18] | Quinn J B,Quinn G D.J Mater Sci,1997;32:4331 |
| [19] | Sahin O,Uzun O,K (o)lemen U,Düzgün B,Ucar N.Chin Phys Lett,2005;22:3137 |
| [20] | Hays C,Kendall E G.Metallography,1973;6:275 |
| [21] | Bektes M,Uzun O,Aktürk S,Ekinci A E,Ucar N.Chin J Phys,2004;42:733 |
| [22] | Pal T,Kar T.Mater Sci Eng,2003;A354:331 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%