通过SO2气体加速腐蚀实验,利用环境扫描电镜(XL30-FEG-ESEM)、能谱分析(EDAX)和Fourier红外光谱(FTIR)等分析技术,研究了碳钢Q235在湿热SO2气氛中的腐蚀行为和锈巢形成机制.结果表明:Q235在不同浓度SO2中腐蚀速率的变化趋势是不同的.浓度较高时,腐蚀速率随腐蚀时间延长而降低;浓度较低时,腐蚀速率随腐蚀时间延长缓慢增加.提高SO2浓度对锈层中含硫化合物的形成影响不大,但对锈层中氧化物或氢氧化物形成起到促进作用.实验条件下的腐蚀产物均含有FeSO4.7H2O,Fe2(SO4)3.9H2O,γ-FeOOH和无定形的δ-FeOOH,当SO2体积分数大于0.5%时,产物中还出现α-FeOOH.在0.05%SO2气氛中,Q235表面形成锈巢,锈巢内、外的各种元素含量差异很大.
参考文献
| [1] | Wang Z Y.Total Corros Control,1995; 9(4):1(王振尧.全面腐蚀控制,1995;9(4):1) |
| [2] | Lin C,Li X G,Wang G Y.Corros Sci Prot Technol,2004;16:90(林翠,李晓刚,王光雍.腐蚀科学与防护技术,2004;16:90) |
| [3] | Weissenriederz J,Leygraf C.J Electrochem Soc,2004; 151(3):165 |
| [4] | Weissenriederz J,Kleber C,Schreiner M.J Electrochem Soc,2004; 151:497 |
| [5] | Wang J H,Wei F I,Chang Y S.Mater Chem Phys,1997;47:1 |
| [6] | Asami K,Kikuchi M.Corms Sci,2003; 45:2671 |
| [7] | Hoerl S,Mazaudier F,Dillmann Ph,Santarini G.Corros Sci,2004; 46:1431 |
| [8] | Emirates S.Eng Res,2006; 11(1):1 |
| [9] | Oesch S.Corros Sci,1996; 38:1357 |
| [10] | Wang Z Y,Wang C,Han W.Equip Environ Eng,2006;3(5):16(王振尧,汪川,韩薇.装备环境工程,2006;3(5):16 |
| [11] | Lin C.PhD Thesis,University Science and Technology Beijing,Beijing,2004(林翠.北京科技大学博士学位论文,北京,2004) |
| [12] | Qu Q,Yon C W,Cao C N.Acta Metall Sin,2002; 38:1062(屈庆,严川伟,曹楚南.金属学报,2002;38:1062) |
| [13] | Yang X M.Spectrosc Spectral Anal,2006; 26:2047(杨晓梅.光谱学与光谱分析,2006;26:2047) |
| [14] | Persson D,Leygraf C.J Electrochem Soc,1993; 140:1257 |
| [15] | Yang X M.Ningxia Univ (Nat Sci),1999; 20:47(扬晓梅.宁夏大学学报(自然科学版),1999;20:47) |
| [16] | Leidheiser H,Music S.Corros Sci,1982; 22:1089 |
| [17] | Singh A K,Ericsson T,Gullman J.Corros Sci,1985; 25:931 |
| [18] | Misawa T,Kyuno T,Suetaka W.Corros Sci,1971; 11:35 |
| [19] | Cox A,Lyon S B.Corros Sci,1994; 36:1177 |
| [20] | Liu X C,An C Q.The Corrosion of Metal.Beijing:National Defence Industry Press,2002:229(刘秀晨,安成强.金属腐蚀学.北京:国防工业出版社,2002:229) |
| [21] | Lyon S B,Thomson G E,Johnson J B.Corrosion,1987;43:719 |
| [22] | Philip A,Schweitaer P E.Atmospheric Degradation and Corrosion Control.New York:Marcel Dekker Inc Press,1999:42 |
| [23] | Graedel T E,Frankenthal R.P.J Electrochem Soc,1990,137:2385 |
| [24] | Marcus P,Oudar J.Corrosion Mechanism in Theory and Practice.New York:Marcel Dekker Inc Press,2002:54 |
| [25] | Leygraf C,Graedel T.Atmospheric Corrosion.New York:John Wiley & Sons Press,2000:72 |
| [26] | Cox A,Lyon S B.Corros Sci,1994; 36:1193 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%