在2Cr13不锈钢中引入TiC颗粒后,室温强度有大幅提高,但塑性和冲击韧性却发生了较大幅度的下降.原位合成的TiC颗粒,尺寸较大且有轻微团聚现象,导致了在拉伸和冲击过程中颗粒易破碎,断裂机制足以TiC增强体失效为主;对TiC强化2Cr13进行电渣重熔后,综合性能得到了改善,TiC颗粒变小且分布变均匀,在拉伸和冲击过程中颗粒不易破碎,断裂机制是以TiC与基体的界面失效为主.
参考文献
| [1] | Warren R.Mater Sci,1980;15:2489 |
| [2] | Dufour L C.Surface and Interface of Ceramic/Metal Materials.London:Kluwer Academic Publisher,1989:393 |
| [3] | Chen J,Wang Z F,Bian J H,Wang X M.Acta Metall Sin,2001;37:207(陈俊,王执福,边建华,王晓明.金属学报,2001;37:207) |
| [4] | Pagounis E,Lindroos V K.Mater Sci Eng,1998;A246:221 |
| [5] | Wu Q L,Sun Y S,Yang C D.Mater Trans.2006;47:2393 |
| [6] | Wu R J.Acta Metall Sin,1997;33:79(吴人杰.金属学报,1997,33:79) |
| [7] | Wang Q P,Yao M,Chen G.J Jiangsu Univ,2003;24:57(王庆平,姚明,陈刚.江苏大学学报(自然科学版),2003;24:57) |
| [8] | Sun Y S,Huang H B,He H Y,Cai L,Xue F,Mei J P.Wang S Q.China Pat ZL99114272.1,2002(孙扬善,黄海波,何华英,蔡磊,薛烽,梅建平,王仕勤.中国专利ZL99114272.1,2002) |
| [9] | Lucia F,Dunitrescu S,Hillert M.ISIJ Int,1999;39(1):84 |
| [10] | Hernandez-Morales B,Mitchell A.Ironmak Steelmak,1999;26:423 |
| [11] | Ma J G,Huang M P,You X Q,Ren H,Si T Z.Spec Cast Nonferrous Alloys,2005;25:16(马建国,黄曼平,尤显卿,任昊,斯庭智.特种铸造及有色合金.2005;25:16) |
| [12] | Singh P M,Lewandowski J J.Metall Trans,1993;24A:2531 |
| [13] | Corbin S F,Wilkinson D S.Acta Metall Mater,1994;42:1329 |
| [14] | Clyne T W,Withers P J(eds.),Yu Y N,Fang Z G(trans.).Metal Matrix Composite.Beijing:Metallurgical IndustryPress,1996:26(克莱因T W,威瑟斯P J著,余永宁,房志刚译.金属基复合材料导论.北京:冶金工业出版社,1996:26) |
| [15] | Sun J R.PhD Thesis,Southeast University,Nanjing,2001(孙建荣.东南大学博士学位论文,南京,2001) |
| [16] | Wang L,Niinomi M,Takahashi S,Hagiwara M,Emura S,Kawabei Y,Kim S J.Mater Sci Eng,1999;A263:319 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%