建立了底吹钢包内气/钢液/渣三相流动数学模型,利用多相流动体积法(VOF)模拟了渣层运动行为.模型结果再现了底吹钢包内气/钢液/渣三相流动现象.当Ar气被吹进钢包时,在钢液内产生气泡,上升的气泡间歇地冲击并突破渣层,产生渣眼;同时,渣层发生波动,波动频率随着Ar气流量的增加而增加.参数研究显示:220t钢包底吹流量由100增加到300 L/min,渣眼直径由0.43增加到0.81m.计算的无量纲渣眼面积与文献中渣眼的实验结果很接近.Ar气喷吹期间,渣层发生重大的变形,近渣眼处的渣层变薄,近钢包壁处的渣层变厚.渣眼周围钢液流速很大,并导致部分渣滴卷入钢液中.
参考文献
| [1] | Ridenour P,Yin H B,Balajee S R,Chaubal P,Zhou Q.In:Ashburn R E ed.,AIS Tech 2006-Proceedings of the Iron and Steel Technology Conference,Cleveland,Ohio,2006:721 |
| [2] | Beskow K,Dayal P,Bjorkvall J,Nzotta M,Sichen D.Ironmak Steelmak,2006;33:74 |
| [3] | Lachmund H,Xie Y K,Buhles T,Pluschkell W.Steel Res Int,2003;74:77 |
| [4] | Han J W,Heo S H,Kam D H,You B D,Park J J,Song H S.ISIJ Int,2001;41:1165 |
| [5] | Jonsson L,Sichen D,J(o)nsson P ISIJ Int,1998;38:260 |
| [6] | Krishnapisharody K,Irons G A.Metall Mater Trans,2006;37B:763 |
| [7] | Yonezawa K,Schwerdtfeger K.Metall Mater Trans,1999;30B:411 |
| [8] | Jonsson L,Jonsson P.ISIJ Int,1996;36:1127 |
| [9] | Hirt C W,Nichols B D.J Comput Phys,1981;39:201 |
| [10] | Li B K,He J C,Lu Z W.Acta Metall Sin,1993;29:143(李宝宽,赫冀成,陆钟武.金属学报,1993;29:143) |
| [11] | Mazumdar D,Guthrie R I L.ISIJ Int,1995;35:1 |
| [12] | Mazumdar D,Guthrie R I L.Metall Trans,1995;25B:308 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%