采用动电位扫描、交流阻抗电化学方法和慢应变速率拉伸实验(SSRT)研究了CO2对X70管线钢在库尔勒土壤模拟溶液中应力腐蚀开裂(SCC)行为的影响,并利用扫描电镜分析了不同CO2分压下的断面形貌.结果表明:CO2能够与腐蚀膜FeCO3反应,生成可溶性Fe的络合物Fe(CO3)2-2,加速X70管线钢腐蚀;CO2与H2O形成H2CO3和HCO-3,为阴极反应提供H+.X70管线钢在含CO2溶液中的SCC机理为氢脆-阳极溶解协同机理,且随CO2分压的增加,氢脆作用增大.
参考文献
| [1] | Albarran J L,Aguilar A,Marttinez L,Lopez H F.Corrosion,2002;58:783 |
| [2] | Koh S U,Kim J S,Yang B Y,Kim K Y.Corrosion,2004;60:244 |
| [3] | Eadie R L,Szklarz K E,Sutherby R L.Corrosion,2005;61:167 |
| [4] | Zhao M C,Yang K.Scr Mater,2005;52:881 |
| [5] | Yu F,Gao K W,Su Y J,Li X,Qiao L J,Chu WY,Lu M X.Mater Left,2005;59:1709 |
| [6] | Parkins R N,Zhou S.Corros Sci,1997;39:159 |
| [7] | Parkins R N,Zhou S.Corros Sci,1997;39:175 |
| [8] | Niu L,Cheng Y F.Appl Surf Sci,2007;253:8626 |
| [9] | Li M C,Cheng Y F.Electrochim Acta,2007;52:8111 |
| [10] | Contreras A,Albiter A,Salazar M,Perez R.Mater Sci Eng,2005;A407:45 |
| [11] | Parkins R N,Beavers J A.Corrosion,2003;59:258 |
| [12] | Li M C,Cheng Y F.Electrochim Acta,2008;53:2831 |
| [13] | Gu B,Luo J,Mao X.Corrosion,1999;55:96 |
| [14] | Gonzalez-Rodriguez J G,Casales M,Salinas-Bravo V M,Albarran J L,Martinez L.Corrosion,2002;58:584 |
| [15] | Park J J,Pyun S I,Na K H,Lee S M,Kho Y T.Corrosion,2002;58:329 |
| [16] | Li X G,Du C W,Liu Z Y.Corrosion Behavior and Eexpremential Study of X70.Beijing:Science Press,2006:13(李晓刚,杜翠薇,刘智勇.X70管线钢的腐蚀行为与试验研究.北京:科学出版社,2006:13) |
| [17] | Linter B R,Burstein G T.Corros Sci,1999;41:117 |
| [18] | Liu X,Mao X.Scr Metall Mater,1995;33:145 |
| [19] | Cheng Y F.J Mater Sci,2007;42:2701 |
| [20] | Liu J H,Li D,Liu P Y,Guo B L.J Mater Eng,2005;(2):3O(刘继华,李荻,刘培英,郭宝兰-.材料工程,20o5;(2):30) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%