采用药芯焊丝法制得Ni-Al-Cr3C2复合焊丝,将该焊丝堆焊于DZ125合金表面.在氩弧物理热的作用下,Ni与Al化合成Ni3Al并释放大量反应热;Cr3C2发生分解,并在随后凝固过程中重新析出细小的富Cr的M3C2和MrC3相.受冷却速率的影响,靠近母材区域的碳化物尺寸小于外层区域.母材合金元素进入焊接熔池中,发生一系列碳化和氧化反应,生成的化合物按自由能高低随温度降低顺序析出,导致在焊接熔合区形成大量富Hf,Ta,Ti和W的MC复合碳化物和少量氧化物,距焊层表面越近,数量越少直至消失.
参考文献
| [1] | Xu X Y.PhD Thesis,Beijing University of Technology,2001(徐向阳.北京工业大学博士t学位论文,2001) |
| [2] | Sikka V K,Deevi S C,Viswanathan S,Swindem R W,Santella M L.Intermetallics,2000;8:1329 |
| [3] | Blau P J,Devore C E.Tribology Int,1990;23:226 |
| [4] | Compilatory Group of Machine-Producing Technology and Material.Handbook of Machine-Producing Technology and Material(Second Part).Beijing:China Machine Press,1993:674(下册).北京:机械工业出版社,1993:674) |
| [5] | Li S P,Feng D,Luo H L,Zhang X E,Cao X.J Iron Steel Res Int,2006;13(5):37 |
| [6] | Li S P,Feng D,Luo H L.Surf Coat Technol,2007;201:4542 |
| [7] | Li S P,Luo H L,Feng D,Cao X,Zhang X E.Aeta Metall Sin,2007;43:439(李尚平,骆合力,冯涤,曹栩,张喜娥.金属学报,2007;43:439) |
| [8] | Hu J,Li D Y,Llewellyn R.Wear,2005;259:6 |
| [9] | Yilmaz O,Buytoz S.Compos Sci Technol,2001;61:2381 |
| [10] | Chen R Z,She L,Zhang H W,Wang L B.J Aeronaut Mater,2000;20(4):14(陈荣章,佘力,张宏炜,王罗宝.航空材料学报,2000;20(4):14) |
| [11] | Ying R C.Principle of Molten Welding and Metal Welding.Beijing:Machine Industry press,2006:79(英若采.熔焊原理及金属材料焊接.北京:机械工业出版社,2006:79) |
| [12] | Deevi S C,Sikka V K.Intermetallics,1997;5:17 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%