研究了激光烧结工艺条件下微/纳米Cu-W粉体致密化的过程及对显微组织的影响.结果表明,合理增加激光功率或降低扫描速率,可提高烧结致密度及组织均匀性;降低扫描间距至0.15 mm,可改善烧结表面光洁度;铺粉厚度降至0.15 mm,可提高烧结层间结合性.经工艺优化,最高成形致密度达到95.2%,且在烧结组织中形成一系列规则的W环/Cu芯结构;并探讨了该结构的成形机制.
参考文献
| [1] | Guo G C.Liquid Phase Sintering Powder Metallurgy Materials.Beijing:Chemical Industry Press,2003:97(郭庚辰.液相烧结粉末冶金材料.北京:化学工业出版社,2003:97) |
| [2] | Fan J L,Huang B Y,Wang D L,Qu X H,Zhang C F.Rare Met Mater Eng,2001;30:401(范景莲,黄伯云,汪登龙,曲选辉,张传福.稀有金属材料与工程,2001;30:401) |
| [3] | Liu B B,Lu Y N,Xie J X.Chin J Nonferrous Met,2007;17:1410(刘彬彬,鲁岩娜,谢建新.中国有色金属学报,2007;17:1410) |
| [4] | Zhou Z J,Ge C C,Li J T.Acta Metall Sin,2000;36:655(周张健,葛昌纯,李江涛.金属学报,2000;36:655) |
| [5] | da Costa F A,da Silva A G P,Gomes U U.Powder Technol,2003;134:123 |
| [6] | Johnson J L,Brezovsky J J,German R M.MetaU Mater Trans,2005;36A:1557 |
| [7] | Johnson J L,Brezovsky J J,German R M.MetaU Mater Trans,2005;36A:2807 |
| [8] | Hong S H,Kim B K.Mater Lett,2003;57:2761 |
| [9] | Yoon E S,Lee J S,Oh S T,Kim B K.Int J Refract Met Hard Mater,2002;20:201 |
| [10] | Gu D D,Shen Y F,Fang S Q,Xiao J.J Alloys Compd,2007;438:184 |
| [11] | Liu J H,Shi Y S,Lu z L,Huang S H.Appl Phys,2007;89A:743 |
| [12] | Lin X,Yang H O,Chen J,Huang W D.Acta Metall Sin,2006;42:361(林鑫,杨海欧,陈静,黄卫东.金属学报,2006;42:361) |
| [13] | Yan M,Zhang S Q,Wang H M.AetaMetall Sin,2007;43:472(颜敏,张述泉,王华明.金属学报,2007;43:472) |
| [14] | Dong C,Zhang S Q,Li A,Wang H M.Acta Metall Sin,2008;44:598(董犟,张述泉,李安,王华明.金属学报,2008;44:598) |
| [15] | Williams J M,Adewunmi A,Schek R M,Flanagan C L,Krebsbach P H,Feinberg S E,Hollister S J,Das S.Biomaterials,2005;26:481 7 |
| [16] | Kim D G,Lee B H,Oh S T,Kim Y D,Kang S G.Mater Sci Eng,2005;A395:333 |
| [17] | Hong S H,Kim B K,Munir Z A.Mater Sci Eng,2005;A405:325 |
| [18] | Yang M C,Song Z Z,Lu K.Acta MetaU Sin,2004;40:639(杨明川,宋贞祯,卢柯.金属学报,2004;43:639) |
| [19] | Gu D D,Shen Y F.Acta Metall Sin,2007;40:968(顾冬冬,沈以赴.金属学报,2007;43:968) |
| [20] | Simchi A,Pohl H.Mater Sci Eng,2003;A359:119 |
| [21] | Gu D D,Shen Y F.Metall Mater Trans,2006;37B:967 |
| [22] | Arafune K,Hirata A.J Cryst Growth,1999;197:811 |
| [23] | Teng X Y,Min G H,Liu H L,Shi Z Q,Wang H R,Ye Y F.Mater Sci Techn01.2001;9:383(滕新营,闵光辉,刘含莲,石志强,王焕荣,叶以富.材料科学与工艺,2001;9:383) |
| [24] | Yuan Z F,Ke J J,Li J.Surface Tension of Metals and Alloys.Beijing:Science Press,2006:29(袁章福,柯家骏,李晶.金属及合金的表面张力.北京:科学出皈社,2006:29) |
| [25] | Shi L K,Gao S Y,Xi M Z,Ji H Z,Zhang Y z,Du B L.Acta Metall Sin,2006;42:449(石力开,高士友,席明哲,纪宏志,张永忠,杜宝亮,金属学报,2006;42:449) |
| [26] | Anestiev L A,Froyen L.J Appl Phys,1999;86:4008 |
| [27] | Niu H J,Chang I T H.ScrMater,1999;41:25 |
| [28] | Fischer P,Romano V,Weber H P,Karapatis N P,Boillat E.Glardon R.Acta Mater,2003;51:1651 |
| [29] | The Chinese Society for Metals,The Nonferrous Metals Society of China.Handbook of Physical Properties of Metal Materials,Vol.1:Physical Properties of Metals and Testing Methods.Beijing:Metallurgical Industry Press.1987:323(中国金属学会,中国有色金属学会.金属材料物理性能手册(第1册:金属物理性能及测试方法).北京:冶金工业出版社,1987:323) |
| [30] | Yang S M,Tao W Q.Heat Transfer.3rd Ed.,Beijing:Higher Education Press,1998:424(杨世铭,陶文铨.传热学.第3版,北京:高等教育出版社,1998:424) |
| [31] | Chatterjee A N,Kumar S,Saha P,Mishra P K,Choudhury A R.J Mater process Technol,2003;136:151 |
| [32] | Yin H B,Emi T.Metall Mater Trans,2003;34B:483 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%