研究了喷射成形大尺寸La62Al15.7(Cu,Ni)22.3非晶合金在过冷液相区内的塑性变形行为.结果表明,随加热温度的增加和应变速率的减小,该非晶合金由非稳态变形向单一稳态变形行为转变.当应变速率为5×10-3S-1,温度为443 K和挤压比为6.25时,喷射成形La62Al15.7(Cu,Ni)22.3非晶合金样品的密度由挤压前的5.723增加到挤压后的5.924 g/cm3,达到了同成分吸铸态非晶合金密度(6.134 g/cm3)的96.6%.挤压后非晶合金样品依然保持完全非晶态.
参考文献
| [1] | Dong T Y,Yang B,He J P,Zhang Y.Acta Metall Sin,2008; 44:652(董亭义,杨滨,何建平,张勇.金属学报,2008;44:652) |
| [2] | Zhang Y,Tan H,Li Y.J Non-Cryst Solids,2006; 352:3942 |
| [3] | Jiang Q K,Zhang G Q,Chen L Y,Wu J Z,Zhang H G,Jiang J Z.J Alloys Compd,2006; 424:183 |
| [4] | Zhang Y,Xu W,Tan H,Li Y.Acta Mater,2005; 53:2607 |
| [5] | Chan K C,Chen Q,Liu L.Intermetallics,2007; 15:500 |
| [6] | Li J F,Cao Q P,Hu Y,Horsewell A,Jiang J Z,Zhou Y H.Mater Sci Eng,2007; A457:94 |
| [7] | Chu J P,Chiang C L,Wijaya H,Huang R T,Wu C W,Zhang B,Wang W H,Nieh T G.Scr Mater,2006; 55:227 |
| [8] | Shen J,Wang G,Sun J F,Chen D M,Xing D W,Zhou B D.Acta Metall Sin,2004; 40:518(沈军,王刚,孙剑飞,陈德民,邢大伟,周彼德.金属学报,2004;40:518) |
| [9] | Wu S D.The Principle of Metal Superplastic Formation.Beijing:National Defense Industry Press,1997:9(吴诗停.金属超塑性变形理论.北京:国防工业出版社,1997:9) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%