通过在Gleeble 1500热模拟试验机上进行的单轴热压缩实验并结合SEM和EBSD分析技术,研究了共析钢在A1-A(r1)和A1-A(c1)温度范围内的两阶段变形对缓冷组织的影响.结果表明:共析钢在A1-A(r1)温度范围内进行过冷奥氏体形变后,在A1-A(c1)温度范围内再变形时,可以利用应变量控制再奥氏体化进程,在一定应变量下获得奥氏体与未溶渗碳体粒子的混合组织,在随后的缓冷过程中发生离异共析转变,获得超细化(α+θ)复相组织,其中α-Fe平均晶粒尺寸小于3 μm,θ-Fe3C粒子平均尺寸小于0.5μm.

参考文献

[1] Oyama T,Sherby O D,Wadsworth J,Walser B.Scr Met-all,1984;18:799
[2] Sherby O D.ISIJ Int,1999;39:637
[3] Sherby OD,Walser B,Young CM,Cady EM.Scr Metall,1975;9:569
[4] Walser B,Sherby O D.Metall Trans,1979;10A:1461
[5] Wadsworth J,Lin J H,Sherby O D.Met Technol,1981;8:190
[6] Sherby O D,Oyama T,Kum D W,Walser B,Wadsworth J.J Met,1985;37(6):50
[7] Syn C K,Lesuer D R,Sherby O D.Metall Mater Trans,1994;25A:1481
[8] Langford G.MetaU Trans,1977;8A:861
[9] Fu W,Furuhara T,Maki T.ISIJ Int,2004;44:171
[10] Puruharn T,Mizoguchi T,Maki T.ISIJ Int,2005;45:392
[11] Lupton D F,Warrington D H.Met Sci J,1972;6:200
[12] Kaspar R,Kapellner W,Lang C.Steel Res,1988;59:492
[13] Huang Q S,Li L F,Yang W Y,Sun Z Q.Acta Metall Sin,2007;43:724(黄青松,李龙飞,杨王玥,孙祖庆.金属学报,2007;43:724)
[14] Li L F,Yang W Y,Sun Z Q.Metall Mater Trans,2007;39A:624
[15] Chen W,Li L F,Yang W Y,Sun Z Q.Acta Metall Sin,2009;45:151(陈伟,李龙飞,杨王玥,孙祖庆.金属学报,2009;45:151)
[16] Xu P G,Tomota Y.Acta Metall Sin,2006;42:681(徐平光,友田阳.金属学报,2006;42:681)
[17] HondaK,Saito S.J Iron Steel Inst,1920;102:261
[18] Whiteley J H.J Iron Steel Inst,1922;105:339
[19] Payson P,Hodapp W L,Leeder J.Trans ASM,1940;28:306
[20] Grossmama MA,Bain EC.Principles of Heat Treatment.5th ed.,Ohio:American Society for Metals,1964:201
[21] Cullen O E.Met Prog,1953;64:79
[22] Parusov V V,Dolzhenkov I I,Sukhomlin V I.Met Sci HeatTreatment,1985;27:402
[23] Verhoeven J D,Gibson E D.Metall Mater Trans,1998;29A:1181
[24] Sun Z Q,Yang W Y,Qi J J,Hu A M.Mater Sci Eng,2002;A334:201
[25] Yang W Y,Qi J J,Sun Z Q,Yang P.Acta Metall Sin,2004;40:135(杨王玥,齐俊杰,孙祖庆,杨平.金属学报,2004;40:135)
[26] Tsuzald K,Sato E.Furimoto S,Puruhara T,Maki T.ScrMater,1999;40:675
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%